Abstract
The micro particle,s shapes of the magnetic films obtained by electrode position of Iron ions and Cobalt-Iron mixed ions in aluminum anodic oxidized films are dependent on the size of particle diameter. When the diameter of deposited particles is larger than $300\AA$, the film plane anisotropy caused by bottom extremity increases, and the crystalization orientation of FeC deposited unusually in the part of the bottom extremities affects on the coercive force Hc and the magnetic anisotropy energy Ku. It was confirmed that the shape anisotropy of particle affects on the both Hc and Ku because the FeC did not deposit in the Iron deposited samples entirely, but in the Cobalt-Iron alloy deposited samples, the effects by the very strong crystalization orientation of the FeC is larger than that of the shape anisotropy. From these results, the Cobalt-Iron alloyed films could switchover the film plane magnetic anisotropy to the perpendicular magnetic anisotropy energy by using the constrainting method of FeC deposition with Cu deposition instead of Cobalt-Iron alloy in the bottom extremities.
양극산화피막에 철이온 및 코발트-철혼합이온 등을 전해석출하여 얻어지는 자성막의 입자는, 입자의 크기 Dp에 따라 모양이 크게 달라진다. Dp가 $300\AA$ 이상일때 나무가지모양의 초기석출부가 반드시 생성된다. 이것은 초기석출부의 형상만을 고려할때 자성막의 국부적충진율을 증가시킴으로, 철석출막의 경우와 같이 항자력 Hc 및 수직자 기이방성 Ku의 감소효과를 가져온다. 코발트-철합금 석출막의 경우, 일부조성에서 초기석출부의 형상효과보다는 여기에 석출한 FeC의 결정배향이 더 크게 작용하여, Hc의 감소와 -Ku를 나타내었다. 이러한 초기석출부의 영향이 규명됨에 따라 코발트-철합금 자성막의 제작시 초기석출부의 FeC석출을 억제시키는 방법을 사용, 임의의 조성에서 수직자기이방성을 갖게하는 것이 가능하였다.