Magnetic Properties of (Fe, Co)-Al-B-Nb Nanocrystalline Alloys on Composition and Annealing Temperature

(Fe, Co)-Al-B-Nb 초미세결정립합금의 조성 및 열처리온도에 대한 자기적 특성변화

  • 강대병 (충남대학교 공과대학 금속공학과) ;
  • 김택기 (충남대학교 공과대학 금속공학과) ;
  • 조용수 (한국표준과학연구원)
  • Published : 1995.02.01
Download PDF
⟨ Previous Next ⟩

Abstract

${(Fe_{0.85}Co_{0.15})}_{75}Al_{7}B_{18-x}Nb_{x}(x=2,\;4\;and\;6\;at%)\;and\;{(Fe_{0.85}Co_{0.15})}_{75}Al_{y}B_{21-y}Nb_{4}(y=3,\;5,\;7,\;9\;at%)$ alloys were prepared by a single-roll quenching method. Microstructure and magnetic properties of the alloys such as saturation magnetization, initial permeability, coercive force and power loss have been investigated as functions of composition and armea1ing temperature. Nanocrystallines are obtained by armealing of as-prepared amorphous alloys in all compositions except the alloy of 9 at% AI. Saturation magnetization increases after armea1ing and, decreases with Nb content. However, AI and B affects the saturation magnetization insignificantly. Initial perrreability of nanocrystallized alloy at 50 kHz is improved roore than twice compared to that of the as-prepared alloy. Coercive force and core loss reach less than half after armea1ing.

급속응고법중 단롤법을 이용하여 Fe-B계에 Co 및 Nb과 Al이 치환된 (Fe/sub 0.85/Co/sub 0.15/)/sub 75/ Al/sub 7/B/sub 18-x/Nb/sub x/(x = 2, 4, 6)와 (Fe/sub 0.85/Co/sub 0.15/)/sub 75/Al/sub y/B/sub 21-y/Nb/sub 4/ (y = 3, 5, 7, 9)합금을 급속응고장치로 단롤법을 이용하여 리본상으로 제작한후, 이들 합금의 초미세결정립 제조 가 능성과 자기적 특성의 조성 및 온도 의존성을 조사하였다. 초미세결정립합금은 y = 9를 제외한 전조성에서 제조가 가 능하였다. 포화자화 값은 열처리 후 증가하였고 Nb 함량이 증가하면 감소하였으며 상대적으로 Al과 B의 영향은 적었 다. 50 kHz에서 조사한 초투자율은 초미세결정립이 형성된 후가 열처리 전보다 2배이상 증가하였으며, 항자력과 교류 자기이력손실은 반대로 1/2이하로 감소하였다.