Gibbsite 를 이용한 대체 차수재 개발 타당성 연구 - Batch Test를 통한 흡착실험을 중심으로 -

This study investigates the adsorption capacity of the gibbsite and the clay on the development of admixed liner. The gibbsite is produced as a by-product in the pretreatment process for cleaning and coloring of Alurninurn sash. From the study, following conclusions were obtained: 1) The adsorption of metals such as Cu(II), Cd(II), and Ni(II) and phenol on gibbsite and l:entonite was equilibrated rather quickly(12 ~48 hrs ). 2) The rate and extent of adsorption is a function of surface area the adsorbent having. 3) The Larigmuir isotherm is found to be more suitable than Freundlich isotherm for the adsorption analysis of heavy metals on gibbsite and bentonite. 4) In case of phenol, Freundlich isotherm, whose N value is close to 1, i.e., close to linear isotherm, is more fit to describe the adsorption on gibbsite and bentonite. 5) The amount of metals and phenol adsorbed is found to be in the following order : Adsorbent : $2{\mu}m-Al(OH)_3$ > Mixed Solid > $12{\mu}m-Al(OH)_3$ > Na-Bentonite > $30{\mu}m-Al(OH)_3$

본 연구는 혼합차수재 개발의 일부로 알루미늄 샛쉬 제작공정에서 산업 부산물로 생산되고 있는 gibbsite 와 자연 생성물인 점토광물이 흡착능을 조사한다. 연구결과는 다음과 같이 몇 가지로 요약할 수 있는데, 1) 구리, 카드뮴, 니켈, 페놀등의 흡착은 12 시간에서 48 시간 이내로 비교적 신속히 평형을 이루었다. 2) 흡착은 표면현상으로 흡착의 속도와 범위는 흡착제의 비표면적과 밀접한 관계가 있다. 3) Gibbsite 와 bentonite 표면에서 중금속의 흡착현상은 Freundich 등온흡착식 보다 Langmuir 등온흡착식의 적용이 보다 타당하였다. 4) 페놀의 경우 N 값이 1 에 가까운, 즉 선형 등온흡착식과 유사한 Freundich 식이 흡착해석에 유리하였다. 5) 중금속과 페놀은 다음 순서로 더 많은 흡착제거가 이루어 졌다. 흡착제 : $2{\mu}m-Al(OH)_3$ > 혼합시료 > $12{\mu}m-Al(OH)_3$ > Na-벤토나이트> $30{\mu}m-Al(OH)_3$