Ampicillin sodium (AMP-Na) was loaded Into fibrin glue (FG) in two different ways and was tried to achieve sustained release from FG. One was loading of AMP-Na in a simple mixing and the other was loading of bovine serum albumin (BSA) microspheres which contained ANP-Na. In case of simple mixing, the release control of AWP-Na from FG was tried by variation of FBNG concentration, but failed. However, the loading of BSA mlcrosphere containing ANP-Na into FG showed sustained re- lease of AMP-Na, especially when microsphere was crosslinked with glutaraldehyde (tO.9 : 33hr). The maximum adhesive strength of FG showed at concentration of FBWG and thrombin, 5.0 % and 25-50 NIHU/ml, respectively. The concentration of Factor Xlll (0-500 U/1g of FBNG) did not affect the adhesive strength of FG. The optimal incubation time was 60 min. The AMP-Na or BSA microsphere which was loaded into FG had no significant effect on the adhesive strength of FG.
광범위 항생물질인 Ampicillin sodium(AMP-Na)을 두가지 방법 즉, 단순섞임과 bovine serum albumin(BSA)으로 microsphere화한 후 loading 하는 방법으로 fibrin glue(FG)를 제조하였고 이 FG로부터 AMP-Na의 서방성 시험을 시도하였다. 단순섞임의 경우 fibrinogen(FBNG)의 농도를 조적함으로서 FG로부터 AMP-Na의 지속적 방출을 달성할 수 있었으며 특히 이 microsphere를 glutaraldehyde로 가교화시킴으로서 용출속도를 더욱 늦출 수 있었다.(tO.9 : 33hr). FG의 rat perironeum에 대한 접착력은 FBNG과 thrombin의 농도가 각각 5.0%, 25~50 NIHU/ml에서 최대로 나타났다. Factor XIII의 농도는 0~500 U/1g of FBNG의 범위내에서 접착력에 거의 영향을 미치지 않았으며 incubation time은 60분일 때 최대로 나타났다. FG에 AMP-Na 및 BSA micorsphere를 loading하여도 접착력에는 큰 영향을 미치지 않았다.