Studies on the Press Drying and the Chemical Absorption of the Plywood Treated with Diammonium Phosphate

제2인산(第2燐酸)암모늄 처리합판(處理合板)의 약제흡수(藥劑吸收) 및 열판건조(熱板乾燥)에 관(關)한 연구(硏究)

The plywoods commonly used as decorative interior materials for the construction are inflammable and so it is a causative factor for making fire accidents, resulting in the destruction of human life and personal properties. Indeed, it is, therefore, required to produce fire-retardant plywoods. In this study, a special grade of defect-free, Kapur plywood was used. Specimens were cut into 3- by 20cm dimensions from 120- by 240- by 0.33-cm panels(thin panel) or 120- by 240- by 0.5-cm panels(thick panel). Some specimens were treated with diammonium phosphate(DAP), but some were not treated with diammonium phosphate to use as control panels. Chemical absorption, drying curves, drying rates and dynamic Young's modulus were investigated. The results were summaries as follows; 1. The specimens were soaked into 19% diammonium phosphate solution by a full cell pressure process and the diammonium phosphate retained in the thin and thick plywoods was 1.409kg/$(30cm)^3$, 1.487kg/$(30cm)^3$, respectively. 2. Diammonium phosphate-treated plywoods were redried with press-drying process at one of either condition dried on the platen($115^{\circ}C$) for a period of time or dried on the platen($50^{\circ}C$) for 3 hrs plus in a dry-oven($30^{\circ}C$) for 24 hrs. or dried on the platen($60^{\circ}C$) for 2 hrs plus in a dry-oven($30^{\circ}C$) for 24 hrs. The drying rate of treated thin specimens dried at $60^{\circ}C$ plus $30^{\circ}C$ and $115^{\circ}C$ only was found to be 0.04 %/min. and 8.53 %/min. Similarly, the drying rate of treated thick specimens were 0.03 %/min. and 6.77 %/min. respectively. 3. It was evident that highly-significantly different drying rate of treated plywoods was observed between plywood thicknesses and platen temperatures and the rate was increased by elevating the platen temperature up to $115^{\circ}C$. Based on the two-way variance analysis, highly significant drying rate was observed from the interaction between plywood thicknesses and platen temperatures. 4. After redrying, the specimens were weighed and reconditioned to a constant weight in a facility maintained temperature ($20^{\circ}C$) and relative humidity(65%) prior to test dynamic Young's modulus. The test revealed that the thin specimens dried at the platen temperature of $50^{\circ}C$, $60^{\circ}C$, $115^{\circ}C$ and untreated specimens showed 1.070E+09 dyne/$cm^2$, 1.156E+09 dyne/$cm^2$, 1.243E+09 dyne/$cm^2$, and 1.052E+09 dyne/$cm^2$, respectively. Likewise, the thick specimens revealed 5.647E+09 dyne/$cm^2$ 5.670E+09 dyne/$cm^2$, 6.395E+09 dyne/$cm^2$ and 5.415E+09 dyne/$cm^2$, respectively. 5. It was evident that significantly different dynamic Young's modulus was observed between the plywood thickness and the platen temperature, but not in the two-way interaction between the plywood thickness${\times}$the platen temperature.