수종의 apical plug 재료의 근단 폐쇄성에 관한 실험적 연구

EVALUATION OF APICAL PLUG MATERIALS USED FOR THE CONTROL OF EXTRUSION OF HIGH-TEMPERATURE THERMOPLASTICIZED GUTTA-PERCHA

The purpose of this study is to evaluate of apical plug materials for the contral of extrusion and sealing ability of high-temperature thermoplasticized gutta-percha in plastic root canal blocks. Seventy seven plastic blocks with canal preformed were instrumented with # 50K file 1 mm beyond apical foramen. Blocks were randomly divided into 5 groups of 15 blocks each. Group 1 was filled by high-temperature thermoplasticized gutta-percha only. The another 4 groups were placed with apical plug materials each other and then remaining space was back filled with high temperature thermoplasticized gutta-percha Apical plug materials were used as follows; Group 2: Thermoplasticized gutta-percha (Thermoplasticized gutta-percha group) Group 3 :. Calcium hydroxide powder (Calcium hydroxide group) Group 4 : Silver point (Silver point group) Group 5 : Gutta-percha cone softened by chloroform (Gutta-percha cone group) All the blocks were stored in 100 % relative humidor at room temperature for 14 days. Filling material extruded was removed carefully and then weighed in analytic balance. Each block was placed in centrifuge tube filled with India ink, and then centrifuged for 20 minutes at 3,000 rpm. Apical leakage was measured from the apical foramen to the most coronal level of dye leakage in millimeter by two examiners under a stereoscope. The data were analysed statistically by Student's t-test The obtained results were as follows; 1. The amounts of material extruded through the foramen decreased in all of groups used apical plug materials (P<0.01). 2. Silver point group and gutta-percha cone group were similar linear leakage to high-temperature thermoplasticised gutta-percha technique only (P>0..5). 3. Calcium hydroxide group and thermoplasticized gutta-percha group showed more liner leakage than high-temperature thermoplasticized gutta-percha only (P<0.01, P<0.05). 4. High-temperature thermoplasticized gutta-percha technique with silver point and gutta-percha cone as apical plugs showed less linear leakage and less extrusion of filling material.