The Effect of Mn Content Solution-treatment Temperatures on Insoluble Phases in Al-Li-Cu-Mg-Mn-Zr Alloys

Al-Li-Cu-Mg-Zr 합금의 미고용상에 미치는 용체화 처리 및 Mn 함량의 영향

Large insoluble phases and dispersoids in Al-Li-Cu-Mg-Mn-Zr alloys containing Mn were analyzed with EPMA(Electron Probe Microanalyzer) and SAEM(Scanning Auger Electron Microscope). Morphology, distribution and volume fraction of the large insoluble phase were also analyzed quantitatively by optical microscopy. Mechanical properties were tested at room temperature and at $200^{\circ}C$. With increasing Mn contents, the volume fraction of the large insoluble phases increased steeply, thus decreasing ductility. Mn was found to be very effective for obtaing uniformly distributed fine-grain structures. The alloy containing 0.44 wt% Mn showed the highest tensile strength among Mn-bearing alloys tested.

Mn의 함량을 달리하여 제조한 Al-Li-Cu-Mg-Mn-Zr 합금의 미고용상 및 분산상을 EPMA(Electron Probe Microanalyzer)와 SAEM(Scanning Auger Electron Microscope)으로 분석하였다. 또한 미고용상의 부피 분율, 분포 및 형태를 광학현미경으로 관찰하였으며, 상온과 고온에서의 인장 특성을 조사하였다. Mn의 함량이 증가함에 따라 미고용상의 부피분율을 급격히 증가하고 연신율을 감소하였다. Mn은 기지 조직의 결정립을 미세하고 균일하게 분포하도록 하였다. 인장시험 결과, 0.44 wt% Mn이 첨가된 합금이 다른 합금보다 우수한 기계적 특성을 나타내었다.