Nb-carbonitride Analysis Techniques in Nb-steels

강 중 Nb계 탄질화 석출물 정량분석 기술

  • Lee, J.J. (Analytical lab., Research Institute of Industrial Science & Technology) ;
  • Jung, S.W. (Analytical lab., Research Institute of Industrial Science & Technology) ;
  • Yoo, K.S. (Department of Chemistry, Ulsan University)
  • 이중주 (산업과학기술연구소 분석실) ;
  • 정성욱 (산업과학기술연구소 분석실) ;
  • 유광식 (울산대학교 화학과)
  • Received : 1994.09.29
  • Published : 1994.12.25
Download PDF
⟨ Previous Next ⟩

Abstract

The morphology and structure of precipitates of formed in Nb steels were investigated using SEM, TEM and XRD. The quantitative analysis of the precipitates was performed by ICP-AES. The potentiostatic etching method was employed as an extraction method using 10% AA-methanol and 15% Na-citrate electrolytes. The two selected potentials relative to SCE(Standard Calomel Electrode), -100mV in 10% AA-methanol solution and -250mV in 15% Na-citrate solution were found to be effective for the extraction. XRD analysis showed that composition of Nb carbonitride in Nb-steel(0.01% C-0.7% Nb-0.004N) was $NbC_{0.65}N_{0.2}$.

Nb steel에 있어서의 석출물의 형상과 구조를 SEM, TEM과 XRD를 이용하여 연구하였고 추출물들의 정량분석을 ICP-AES를 사용하여 실시하였다. 석출물 추출 방법으로는 정전위 전해추출법을 사용하였고 전해액으로는 10% AA-methanol 용액과 15% Na-citrate 용액을 사용하여 비교하였다. 전해추출 전위는 10% AA-methanol 용액에서는 -100mV, 15% Na-citrate 용액에서는 -250mV로 선택하였고 이 전위에서 Nb 석출물을 분리하는 데 적당하였다. 추출 잔사 중의 $Fe_3C$의 크기는 $0.2{\sim}1.0{\mu}m$ 정도였고 Nb 탄질화물의 크기는 $0.003{\sim}0.1{\mu}m$ 정도였다. 0.1% C-0.007% Nb-0.004% N의 조성을 가진 강에서 Nb 석출물의 조성은 $NbC_{0.65}N_{0.2}$인 것으로 나타나 입방정계의 탄질화물인 것으로 판명되었다.