$Hg_{1-x}Cd_{x}$Te photovoltaic 대형 적외선 감지 소자의 제작

Fabrication of a Large-Area $Hg_{1-x}Cd_{x}$Te Photovoltaic Infrared Detector

We fabricated a large-scale photovoltaic device for detecting-3-5$\mu$m IR, by forming of n$^{+}$-p junction in the $Hg_{1-x}Cd_{x}$Te (MCT) layer which was grown by LPE on CdTe substrate. The composition x of the MCT epitaxial layer was 0.295 and the hole concentration was 1.3${\times}10^{13}/cm^{4}$. The n$^{+}$-p junction was formed by B+ implantation at 100 keV with a does 3${\times}10^{11}/cm^{2}. The n$^{+}$ region has a circular shape with 2.68mm diameter. The vacuum-evaporated ZnS with resistivity of 2${\times}10^{4}{\Omega}$cm is used as an insulating layer over the epitaxial layer. ZnS plays the role of the anti-reflection coating transmitting more than 90% of 3~5$\mu$m IR. For ohmic contacts, gole was used for p-MCT and indium was used for n$^{+}$-MCT. The fabrication took 5 photolithographic masks and all the processing temperatures of the MCT wafer were below 90$^{\circ}C$. The R,A of the fabricated devices was 7500${\Omega}cm^{2}$. The carrier lifetime of the devices was estimated 2.5ns. The junction was linearly-graded and the concentration slope was measured to be 1.7${\times}10^{17}/{\mu}m$. the normalized detectivity in 3~5$\mu$m IR was 1${\times}10^{11}cmHz^{12}$/W, which is sufficient for real application.