Experimental Study on the Development and Evaluation of Lt.Wt.& High Strength Composites Utilizing By-Products and Calcium Silicates for Construction Materials(1)

산업부산물 및 규산칼슘계 재료를 이용한 건재용 경량.고강도 복합체의 개발.평가에 관한 실험적 연구(기 1)

The results of an experimental study on the development and the evaluation of lightweight and high strength composites utilizing by-products and calcium silicates for construction materials are presented in this paper. The composites using early strength portland cement, by-Products( f1y ash, silica fume), silica powder, quick lime, gypsum, A1 powder and fibers(PAN-derived CF, alkali-resistance GF) were prepared using various mixing conditions. As the test results show, PAN-derived CF and alkali-resistance GF were suitable for rein-forcing fiber of the composites. And the mechanical properties,such as compressive tensile flexural strength, and toughness of Lt. Wt. fiber reinforced calcium silicates cement comp-osites were improved by increasing the fly ash and silica fume contents, and fiber contents, especially by increasing fiber contents the toughness of the composites were remarkably in-creased. Also, compressive tensile flexural strength,and toughness of the composites rein-forcing PAN-derived CF were higher than those of the composites reinforcing alkali-resistance GF..

산업부산물의 플라이애쉬와 실리카흄 및 국내 부존자원이 풍부한 규사분말, 생석회 및 발포용 알루미늄 분말과 취성개선을 위한 보강용 섬유를 사용한 경량 고강도의 시멘트복합체의 개발을 위하여 오토클래브 양생에 의한 열수 알카리분위기에서의 섬유 자체의 열화현상을 조사함과 아울러 배합요인별로 건재용 경량섬유보강 규산칼슘계 시멘트복합에를 제조하여 그 역학적 특성에 관한 연구를 수행하였다. 시험결과, 탄소섬유 및 내알카리성 유리섬유는 보강용 섬유로서 적합함이 확인되었으며, 경량 섬유보강 규산칼슘계 시멘트복합체의 압축, 인장, 휨강도는 플라이애쉬와 실리카흄 혼입율 및 섬유혼입율이 증가함을 따라 증가하는 경향을 나타내었고 또한 섬유혼입율 증가에 따라 현저히 휨인성이 증가하였으며, 탄소섬유보강의 경유가 유리섬유보강의 경우에 비하여 압축, 인장, 휨강도 및 휨인성은 다소 높은 경향을 나타내었다.