Study on the Coercive Field Strenght Noise Depends on The Magnetic Field Annealing Effect of Amorphous Ribbon

비정질 리본의 자기장중 열처리에 의한 보자력 노이즈의 변화에 관한 연구

Magnetic field annealing method has been used to obtain proper hysteresis loop shapes which are useful to a device using amorphous ribbon. In this study, two pairs of Helmhotz coils were used to apply longitudinal and transverse magnetic field during annealing. For the measurement of coercive field strength noise which depends on magnetic field annealing, Co-based amorphous alloy ribbon $VITROVAC^{\circledR}$ 6030 was used. For the sample which was annealed under dc transverse and dc longitudinal magnetic field, coercive field strength noise was nearly independent of magnetizing frequency ranging from 1 to 100 kHz, but dc transverse and ac longitudinal magnetic fields annealed samples show that the coercive field strength noise decreased in power of magnetizing frequency. When magnetic domain nucleation occurred, the coercive field strength noise increased remarkably and decreased in power of magnetizing frequency.

본 연구에서는 2쌍의 헬름홀쯔코일을 사용하여 비본형 시편의 종방향 및 횡방향으로 자기장 을 인가한 상태에서 열처리한 Co-계 비정질 합금 VITROVAC 6030의 보자력 노이즈를 측정하였다. 시편의 종방향 및 횡방향으로 dc 자기장을 인가한 상태에서 열처리한 시편의 경우, 보자력노이즈는 자화주파수 가 1~100 kHz 범위에서 거의 변화하지 않았으며, 시편의 종방향으로 ac 자기장을 횡방향으로는 dc자기 장을 인가한 상태에서 열처리한 시편의 경우의 보자력 노이즈는 자화주파수의 거듭제곱으로 감소하는 경 향을 보였다. 또한 자구핵형성이 일어날 경우 보자력 노이즈는 크게 증가하며 자화주파수의 거듭제곱으 로 감소하는 경향을 보였다.