Abstract
With the variation of Cr content and $N_2$ flow ratio, the soft magnetic properties, corrosion resistance and reactivity of the sputtered nanocrystalline FeZrCrN thin flims were investigated. In case of FeZrCrN thin films, a saturation magnetization was decreased with increasing $N_2$ flow ratio. In addition, good soft magnetic properties were obtained at the flow ratio of 3% $N_2$. The $Fe_{64.9}Zr_{8.8}Cr_{5.8}N_{20.5}$ nanocrystalline thin film after annealing at $550^{\circ}C$ exhibited the saturation magnetization of 12.5kG, low coercivity of 0.4 Oe and high permeability of 2600 at 5 MHz. Films containing up to 7.5% Cr showed an enhanced corrosion resistance and reduced reactivity with the bonding glass without degradation of soft magnetic properties, although the saturation magnetization was decreased slightly with the Cr addtion.
스퍼터방식으로 제조한 FeZrCrN 미결정박막의 질소 유입량의 변화와 Cr 첨가량 변화에 따라 연자기특성과 내반응성 및 내식성을 조사하였다. 질소 유립량 증가에 따라 포화자속밀도는 감소하고 적 절한량(질소 유입량 3%)의 질소가 유입 되었을 때 열처리후에도 이방성 분산 감소효과 등에 의하여 우수 한 연자기특성이 출현 하였으며, 이때 보자력은 0.4 Oe, 투자율은 5 MHz에서 2600 정도를 나타내었다. FeZrN 박막에 Cr을 7.5 at.% 정도 첨가하였을때 포화자속밀도는 12.5kg까지 감소하였지만 양호한 연자기 특성이 그대로 유지되었고 Cr 첨가에 의해 현저한 내식성의 향상과 집합 glass와의 내반응성의 개선이 있었다.