Abstract
Aluminum nitride was hydrolyzed in contact with water, evolving the reaction heat of 172 cal/g within 12 hours to form alumina trihydrates. At 4$0^{\circ}C$ >, amorphous alumina hydrate was easily produced by the spontaneous breaks of AlN particle at the beginning of the hydrolysis process, while bayerite was formed by the dissolution-recrystallization processes of amorphous alumina hydrate at the temperature between 4$0^{\circ}C$ and 6$0^{\circ}C$, and pseudo-boehmite was generated on the surface of AlN particle by the condensation process of the corresponding phase at 6$0^{\circ}C$ <. The longer the hydrolysis timje or the higher the value of pH in solution, the more the bayerite phase was produced. However, pseudo-boehmite was easily generated under the following favorable conditions; when the hydrolysis reaction occured rapidly at the beginning and when the absorption of OH radical on the surface of AlN particle was disturbed by ethyl alcohol in a solution. However, aluminum nitride was hardly hydrolyzed in a solution of pH 2.0.
AIN은 불안정하여 물과 접촉하면 12시간 이내에 172cal/g의 열을 내면서 가수분해되어 알루미나 삼수화물이 생성되었다. AIN의 가수분해 과정은 초기에 비정질 알루미나 수화물이 생성되었으며, 가수분해 조건에 따라 비정질알루미나 수화물의 용해-재석출과정으로 알루미나 삼수화물 특히 bayerite가 생성되었고, 응축과정으로 pseudo-boe-hmite가 AIN 입자표면에 생성되었다. 가수분해 온도 4$0^{\circ}C$ 이하에서는 비정질 알루미나 수화물이, 4$0^{\circ}C$와 6$0^{\circ}C$ 사이에서는 bayerite가 각각 생성되었고, 6$0^{\circ}C$ 이상의 경우는 초기에 pseudo-boehmite의 입자표면에 형성되었다. bayerite는 가수분해 시간이 길수록, 그리고 용액내 pH가 높을수록 잘 생성되었으나 pseudo-boehmite는 가수분해 반응이 급격히 일어날 때와 용액내 ethyl alcohol의 존재로 OH 기의 흡착을 방해하여 가수분해 반응이 억제될 때 잘 생성되었다. 그리고 pH=2.0인 용액에서는 AIN의 가수분해가 거의 일어나지 않았다.