ZnO의 과잉첨가가 Ba(${Zn}_{1/3}{Ta}_{2/3}$)$O_3$세라믹스의 마이크로파 유전특성에 미치는 영향

Effect of Excess ZnO on Microwave Dielectric Characteristics of Ba(${Zn}_{1/3}{Ta}_{2/3}$)$O_3$ Ceramics

Dielectric properties of Ba(ZnS11/3TTaS12/3T)OS13T+x ZnO(x=0, 0.4, 0.8, 1.0 wt%) ceramics have been investigated at microwave frequencies. With excess ZnO, the sinterability was improved and the dielectric constant($\varepsilon$S1rT) and the unloaded quality factor(QS1UT) were increased. The structure changed into hexagonal from pseudocubic as being annealed at 140$0^{\circ}C$ in excess ZnO composition. Also, the temperature coefficient of the resonant frequency ($\tau$S1fT) turned into (-)ppm/$^{\circ}C$ when sintered at 155$0^{\circ}C$ for 2 hours. But the specimen sintered in ZnO muffling showed increased density and $\varepsilon$S1rT but lowerde QS1uT. Among the specimen investigated, expecially the composition added with 0.4wt% excess ZnO showed the most optimum dielectric values ($\varepsilon$S1rT=28, QS1uT x f=120000GHz) better than those of original Ba(ZnS11/2T TaS12/3T)OS13T ceramics.