Abstract
Heparin binders (Cell-PALA) used for selective heparin removal from blood, were prepared by immobilizing a cationic polymer, poly(allylamine) (PALA), onto cellulose substrate by a novel method. Their absorbing capacity for heparin was compared with untreated cellulose control using heparin solution in vitro. The surface areas of obtained heparin binders and untreated cellulose were 1.36 and ($2.56{\mu} g$/$cm^2$, respectively. The amount of bound heparin to PALA immobilized celluloses was determined to be 0.16 - $0.30{\mu}g$/cm, which is much higher than that of untreated cellulose ($0.03{\mu} g$/$cm^2$). These results suggest that Cell-PALA materials can be utilized for a heparin removal system.
혈액으로부터 헤파린을 선택적으로 제거하기 위하여 cellulose 기질에 양이온 고분자인 poly(allylamine)(PALA)을 새로운 방법으로 고정화하여 헤파린 제거제를 제조한 다음 in vitro 헤파린 용액내에서 흡착실험을 행하여, 미처리 cellulose control과의 흡착능을 비교하였다. 제조된 헤파린 제거제와 미처리 cellulose의 표면적은 각각 1.36 및 $2.56m^2$/g로 개질처리된 경우의 표면적이 약 1/2로 감소하였다. 또한 제조된 헤파린 제거제에 흡착된 헤파린의 양은 개질 방법에 따라 0.16~$0.03{\mu} g$/$cm^2$로 미처리 celluose($0.03{\mu} g$/$cm^2$)보다 월등히 우수한 헤파린 흡착능을 나타내었다.