A Study Effect of Mixed Solvents on the Retention of Polystyrenes Using Thermal Field-Flow Fractionation

열장 흐름 분획법에 의한 폴리스티렌의 머무름에 미치는 혼합용매의 영향에 관한 연구

The retention behaviors of polystyrenes influenced by mixed solvents are examined in thermal field-flow fractionation(ThFFF). Experimental data are obtained with polystyrene samples of molecular weights of 35,000, 110,000, 200,000 and 470,000 dissolved in organic solvents. The pure and mixed solvents are tetrahydrofuran(THF), chloroform(CHL), cyclohexane(CH), and benzene(BZ), respectively. The values of retention ratio(R) and thermal diffusion coefficient($D_T$) are measured with change of molecular weight and composition of mixed solvents. Atempts are then made to correlate the measured values with various physicochemical parameters of polymers and solvents. Studies suggest that R is significantly increased with the density of solvent and a good correlation is found between them. $D_T$ values decreases in the mixed solvent having has a higher concentration of poor solvent.

본 연구는 열장 흐름 분획법을 이용하여 혼합 용매에서의 폴리스티렌의 머무름을 측정하고 용매의 조성이 시료의 머무름거동에 미치는 영향을 조사하였다. 시료는 분자량이 35,000, 110,000, 200,000, 470,000인 폴리스티렌을, 이동상은 테드라히드로퓨란(THF), 클로로포름(CHL), 시클로헥산(CH), 그리고 벤젠(BZ)의 단일용매 및 혼합용매를 사용하였다. 시료의 분자량과 혼합용매의 조성의 변화에 따라서 시료의 머무름비와 열확산계수를 측정하였으며, 그 값들을 시료와 용매의 물리화학적인 성질과 연관시켜 설명하였다. 즉, 시료의 머무름비는 이동상의 밀도의 영향을 크게 받으며 이동상의 밀도가 클수록 머무름비가 증가함을 알 수 있었다. 또한 이동상에 포함된 poor 용매의 함량이 증가할수록 열확산계수는 감소하였다.