Abstract
High temperature tensile tests, steady state creep tests, Internal stress tests and creep rupture tests using A17075 alloy( $T_{6}$ ) were performed over the temperature range of 9$0^{\circ}C$~50$0^{\circ}C$ (0.4 $T_{m}$ ~0.85 $T_{m}$ ) and stress range of 0.64~17.2(kgf/$\textrm{mm}^2$). The main results obtained in this paper were as follows. (1) The activation energies for yielding at the temperature of 0.4 $T_{m}$ ~0.75 $T_{m}$ were calculated to be 25.7~36.5kcal/mol, which were nearly equal to the activation energies for creep. (2) At around the temperature of 9$0^{\circ}C$~12$0^{\circ}C$ and under the stress level of 10~17.2(kgf/$\textrm{mm}^2$), and at around the temperature of 200~41$0^{\circ}C$ and under the stress level of 1.53~9.55(kgf/$\textrm{mm}^2$) and again at around the temperature of 470~50$0^{\circ}C$ and under the stress level of 0.62~l.02(kgf/$\textrm{mm}^2$), the applied stress dependence of steady state creep rate $n_{measu}$ measured were, respectively, 3.15, 6.62 and 1.1, which were in good agreement the calculated stress dependence $n_{ealeu}$ obtained by the difference of the applied stress dependence of the Internal stress and the ratio of the internal stress to the applied stress. (3) At the temperature range of 0.4~0.43 $T_{m}$ , and at the temperature range of 0.52~0.75 $T_{m}$ and again at the temperature range of 0.82~0.85 $T_{m}$ , the activation energies $Q_{measu}$ obtained by steady state creep rate, respective, 26. 16, 34.9, 36.2 and 36.1kcal/mol, which were in good agreement with those obtained with the activation energies under constant effective stress and the temperature dependence of Internal stress. (4) At the temperature range of the 0.52~0.73 $T_{m}$ and under the stress level of 1.53~9.55(kgf/$\textrm{mm}^2$), the stress dependence of rupture life(n’) measured was 6.3~6.6, which was in good agreement with the stress dependence of steady state creep rate(n). And at the same condition the activation energy for rupture( $Q_{f}$ ) measured was 32.0~36.9kca1/mol, which was also in good agreement with the activation energy obtained by steady state creep rate ( $Q_{c}$ ). (5) The rupture life( $t_{f}$ ) might be represented by athermal process attributed to the difference of the applied stress dependence of the internal stress and the ratio of the internal stress to the applied stress, and the thermal activated process attributied to the temperature dependence of the internal stress as $t_{f}$ = A'$\sigma$$_{a}$ ｛n(1-d $\sigma$$_{i}$ /d $\sigma$$_{a}$ )/(1-$\sigma$$_{i}$ / $\sigma$$_{a}$ )｝.exp[｛ $Q_{c}$ $^{*}$-( $n_{o}$ R $T^2$/ $E_{(T)}$) (d $E_{(T)}$/dT) - ( $n_{0}$ R $T^2$/ $\sigma$$_{a}$ - $\sigma$$_{i}$ ) (d $\sigma$$_{i}$ /dT)｝/RT]. (6) The relationship betwween Larson-Miller rupture parameter and logarithmic stress was linearly decreased, so creep rupture life of Al 7075 alloy seemed to be predicted exactly with Larson-Miller parameter.meter.