Computerized Analysis of Thermoluminescence from ${\gamma}$-Ray Irradiated $\alpha$-$Al_2$$O_3$

감마선 조사된 $\alpha$-$Al_2$$O_3$의 열자극에 관한 수치해석적인 분석

The complex glow curves were split into isolated glow curves to be calculated the values of kinetic order, activation energy, escape frequency and density of initial trap from the independent glow curves using the mathematical method of thermally stimulated processes. The minimization of the intensity difference between measured and theoretical glow curve was done by the nonlinear least-square program. The results of the fitted curves were almost equal to the actual values of the parameters. Thermoluminescence from gamma ray irradiated ${\alpha}$-Al$_2$ $O_3$ over the range of 300K to 600K was split into six glow curves. The kinetic order, activation energy and escape frequency of first glow curve were obtained as 1, 1.12eV and 6.79X10$\^$12/sec$\^$-1/, respectively, which were similar to the results of other method. Also the parameters of the second and the third glow curve and so forth were calculated.

열자극 과정의 수치해석적인 방법을 이용하여 열자극 세기곡선의 kinetic order, 활성화 에너지, 이탈 진동수 그리고 초기 트랩 밀도를 구하기 위하여 혼합된 열자극 세기곡선으로 분해하였고, 비선형 최소 자승법으로 분해된 열자극 곡선 세기와 측정된 세기의 차이를 최소화시켰다. 감마선 선량계로 사용되고 있는 $\alpha$-Al$_2$ $O_3$ 에감마선을 조사시킨 후 ,300K～600K의 온도 구간에서 측정된 $\alpha$-Al$_2$ $O_3$의 열자극 발광 세기곡선은 정점 온도가 381K, 415K, 441K, 460K, 488K 그리고 506K인 6개의 독립된 열자극 발광세기곡선으로 분해되었으며, 381K의 정점온도를 갖는 분해된 열자극 발광 세기곡선의 kinetic order, 활성화 에너지 그리고 이탈 진동수는 각각 1, 1.12eV 그리고 6.79X$10^{12}$sec$^{-1}$로써, 이 결과는 다른 측정법에 의한 값과 유사하였다.