Abstract
Separate-confinement hetero-structure (SCH) broad area Laser Diodes (LD's) were fabricated from $Al_{0.07}$Ga$_{0.93}$/. As single-quantum-well (SQW) grown by metal organic chemical vapor deposition (MOCVD). Under pulsed operation, we obtained maximum output powers of about 0.8watt/facet and 1.83watt/facet from LD's with 60$\mu$m and 160$\mu$m channel width, respectively, without facet coatings. The differential quantum efficiency of the 60$\mu$m wide LD was about 21.7%/facet and its threshold current density was about 1k [A/cm$^{2}$]. The differential quantum efficiency of the 160$\mu$m wide LD was about 25.6%/facet and its threshold current density was about 1k[A/cm$^{2}$]. The minimum threshold current density of 60$\mu$m wide LD's was 620[A/cm$^{2}$] when the cavity length was 603$\mu$m and the minimum threshold current density of 160$\mu$m wide Ld's was 675[A/cm$^{2}$] when the cavity length was 752$\mu$m. The internal quantum efficienty and the internal loss of both LD's were 92.3% and 18.1cm$^{1}$, respectively.