Characteristics of Silica Coated ${\gamma}-Fe_{2}O_{3}$ with Heat-treatment

열처리에 따른 실리카 피착 ${\gamma}-Fe_{2}O_{3}$의 특성

This paper presents a study on the effects of silica coating in the production of ${\gamma}-Fe_{2}O_{3}$ powders suitable for magnetic recording media. Emphasis has been put on investigating the relationship between the powder characteristics and the effects of silica coating in the heat-treatment stage of ${\gamma}-Fe_{2}O_{3}$ production. After we prepared non-coated ${\gamma}-Fe_{2}O_{3}$ and silica coated ${\gamma}-Fe_{2}O_{3}$ with coating water glass on the surface of goethite and heattreatment process, we compared and investigated powder characteristics. As silica coated layer played a role of preventing the powders from overreduction to metal iron and rapid oxidation, silica coated ${\gamma}-Fe_{2}O_{3}$ showed superior magnetization value due to inhibiting t!1e adulteration of ${\alpha}-Fe_{2}O_{3}$ into the final product. When silica coated layer acted as a sintering restrainer, silica coated ${\gamma}-Fe_{2}O_{3}$ showed high coercivity and specific sur-face area due to good acicularity.

자기기록매체에 적합한 실리카 피착 ${\gamma}-Fe_{2}O_{3}$ 제조에 있어서 실리카 피착의 효과와 영향에 대하여 검토하였다. 특히 ${\gamma}-Fe_{2}O_{3}$ 제조시 열처리단계에 있어서 실리카 피착의 효과와 분말의 특성과의 상관관계를 조사하는데 연구의 중점을 두었다. 수산화철 표면에 무기물질인 실리카성분을 물유리를 사용하여 피착한 시료와 피복하지않은 시료를 후속 열처리하여 ${\gamma}-Fe_{2}O_{3}$를 제조한후 이들 분말의 특성을 조사하였다. ${\gamma}-Fe_{2}O_{3}$에 피복된 실리카 피착층은 환원 시 과환원과 급속한 산화반응을 억제하는 확산장벽으로 작용하여 최종제품내에 ${\alpha}-Fe_{2}O_{3}$의 혼입을 방지하기 때문에 실리카 피복된 ${\gamma}-Fe_{2}O_{3}$는 높은 자화특성을 나타내었다. 또한 실리카 피척층은 소결 억제제로 작용하여 실리카가 피복된 시료의 경우 침상성이 우수하여 높은 보자력과 비표면적을 나타내었다.