Sol-Gel법에 의한 $Li_2O-Al_2O_3-TiO_2-SiO_2$계 다공성 결정화 유리의 제조 : (I) Sol-Gel 방법에 의한 $Li_2O-Al_2O_3-TiO_2-SiO_2$계 다공성 겔체의 제조

Preparation of Glass-Ceramics in $Li_2O-Al_2O_3-TiO_2-SiO_2$ System by Sol-Gel Technique : (I) Preparation of Porous Monolithic Gel in $Li_2O-Al_2O_3-TiO_2-SiO_2$ System by Sol-Gel Method

  • 발행 : 1993.07.01
PDF 다운로드
⟨ 이전 논문 다음 논문 ⟩

초록

It was investigated in this study that a preparation method, activation energy, surface area, pore volume, pore size distribution and DTA analysis of the dry gel in process of producing monolithic porous gel in Li2O-Al2O3-TiO2-SiO2 system by the sol-gel technique using metal alkoxides. Activation energy for gellation according to the variation of water concentration and the kind of catalysts ranged from 10 to 20kcal/mole. Monolithic dry gels were prepared after drying at 9$0^{\circ}C$ when the amount of water for gellation was 4~8 times more than the stoichiometric amount, that was necessary for the full hydrolysis of the mixed metal alkoxide. The specific surface area, the pore volume, the average pore radius of the dried gel at 18$0^{\circ}C$ according to the various kinds of catalyst were about 348~734$m^2$/g, 0.35~0.70ml/g and 10~35$\AA$, respectively. It showed that the dry gels were porous body. As a result ofthe analysis of DTA, it was confirmed that the exothermaic peaks at 715$^{\circ}C$ and 77$0^{\circ}C$ was clue to the crystallization of dried gel.

키워드

참고문헌

  1. J. Non-Cryst Solids v.73 Glasses and Glass-Ceramics from Gels Sumio Sakka
  2. Angew Chem. Int. Ed. Engl. v.10 New Routes to Multicomponent Oxide Glasses H. Dishich
  3. J. Non-Cryst. Solids v.16 Conversion of Monolithic Gels to Glasses in Multicomponent Silicate Glass System C.J. Brinker;S.P. Mukerjee
  4. J. Non-Cryst Solids v.63 Structural Developments during the Gel to Glass Transition N. Tohge;G.S. Moore;J.D. Mackenzie
  5. Ultrastructure Processing of Ceramamics, Glasses and Composites Applications of Sol-Gel Methods for Glass and Ceramics Processing J.D. Mackenzie;L.L. Hench(ed.);D.R. Ulrich(ed.)
  6. J. Non-Cryst. Solids v.93 Shrinkage of Lithium Aluminosilicate Gels during Dring P. Anderson;L.C. Klein
  7. J. Non-Cryst. Solids v.99 Temperature Dependence of the Gelation of Silicon Alkoxides M.W. Colby;A. Osaka;J.D. Mackenzie
  8. J. Amer. Chem. Soc. v.60 Adsorption of Gases in Multimulculer Layers S. Brunauer;P.H. Emmett;E. Teller
  9. Powder Surface Area and Porosity(2nd ed.) S. Lowell;J.E. Shields;B. Scarlett(ed.)
  10. ゾル-ゲル法の 科學(第1版) 作花濟夫
  11. Sol-Gel Technology for Thin Films, Fibers, Preforms, Electronics, and Specially Shapes Monolith Formation from the Sol-Gel Process Masayuki Yamane;Lisa C. Klein(ed.)
  12. J. Amer. Chem. Soc. v.90 Silicic Acid from Tetraethyl Sihcate Hydrolysis: Polymerization and Properties M.W. Bechtold;R.D. Vest;L. Plambec, Jr.
  13. Better Ceramics Through Chemistry Ⅰ The Effect of Hydrolysis Conditions on the Structure and Growth of Silicate Polimer K.K. Keefer;C.J. Brinker(ed.);D.E. Clark(ed.);D.R. Ulrich(ed.)
  14. J. Amer. Chem. Soc. v.62 On a Theory of the van der Waals Adsorption of Gases S. Brunauer;L.S. Deming;W.E. Deming;E. Teller
  15. Sol-Gel Science C. Jeffrey Brinker;George W. Scherer
  16. Adsorption, Surface Area and Porosity, (2nd ed.) S.J. Gregg;K.S.W. Sing
  17. J. Non-Cryst Solids v.63 Monolithic Dried Gels and Silica Glass Prepared by the Sol-Gel Process T. Kawaguchi;H. Hishikura;J. Iura;Y. Kokubu
  18. J. Non-Cryst. Solids v.63 Densification of Monolithic Gels D.M. Krol;J.G. VanLierop
  19. J. Non-Cryst. Solids v.63 Preparation of xNa₂O-(1-x)SiO₂Gels for the Gel-Glass Process: Ⅱ M. Prassas;J. Phalippou;L.L. Hench