Abstract
This is the first reported observation of absorption and emission of glasses with a 4d transition metal ion(rhodium). The optical absorption and photoluminescence spectra, and the lifetimes of rhodium ions in phosphate glasses are interpreted on the basis of strong-field scheme of Sugano-Tanabe diagram. We conclude that rhodium ion is present in its divalent form. $^2 E{\rightarrow}^2 T_1$ and $^2 E{\rightarrow}^2 T_2$ transitions are superimposed and observed at 460 nm. Whereas $^2 T_1{\rightarrow}^2 E$ and $^2 T_1{\rightarrow}^2 E$ transitions are observed at 650 nm and 580 nm, respectively.
이 연구에서는 4d 전이원소인 rhodium 이온을 첨가한 유리의 광학적 특성을 조사하였다. Rhodium이 첨가된 phosphate유리의 광흡수, photoluminescence, 수명시간 등을 측정하고 여기에 Sugano-Tanabe의 strong-field scheme을 적용하여 해석한 결과 phosphate유리 속에서 rhodium은 R$h^{2+}$ 상태로 존재하며 이때 10Dq는 약$20,000cm^1$였다. $^2 E{\rightarrow}^2 T_1$과 $^2 E{\rightarrow}^2 T_2$ 천이에 의한 흡수대는 460nm에 중첩되어 나타나고, $^2 T_1{\rightarrow}^2 E$와 $^2 T_1{\rightarrow}^2 E$천이에 의한 luminescence대는 각각 650nm와 580nm에 나타났다.