Ion-Selectrodes based on Calcium Ferrite

칼슘 페라이트 이온-선택성 막전극

The ion-selectrodes based on calcium ferrite were prepared by mixing calcium oxide with ferric oxide on molar ratio of 0.6:1.4, 0.8:1.2, 1.0:1.0, respectively. The specimens were sintered at $1400^{\circ}C$ for 2hrs in $O_2$ and for 20min in $H_2$ atmosphere. The selectrode sintered in hydrogen atmosphere showed better responded potential and wider range of responded concentration than selectrode sintered in oxygen atmosphere. The ion-selectrodes base on calcium ferrite(0.6:1.4 molar ratio.) showed the highest potential to bivalent cations such as $Ca^{2+}$, $Ba^{2+}$, $Mg^{2+}$, $Zn^{2+}$ and halogen anions such as $I^-$, $Br^-$ in the range of $10^{-1}{\sim}10^{-7}M$. It showed good agreement with theoretical nernstian values.

산화칼슘과 산화철을 0.6:1.4, 0.8:1.2, 1.0:1.0 몰비로 혼합하여 만든 디스크 형태의 시편들을 $1400^{\circ}C$ 산소 분위기와 수소 분위기하에서 각각 소결하였다. 수소 분위기하에서 만든 calcium ferrite 막전극이 산소 분위기하에서 만든 calcium ferrite 막전극 보다 더 우수한 감응전위와 감응농도범위를 나타냈다. 수소 분위기하에서 만든 calcium ferrite ($CaO:Fe_2O_3=0.6:1.4$ 몰비) 막전극은 $Ca^{2+}$, $Ba^{2+}$, $Mg^{2+}$, $Zn^{2+}$와 같은 2가 금속 양이온과 $I^-$, $Br^-$와 같은 할로겐 음이온에 대하여 Nernstian 기울기에 근접한 높은 감응전위를 나타내었다.