Recrystallization Behavior of Mo-1.17 Ti-0.18 Zr-0.06 C Alloy
Mo-1.17 Ti-0.18 Zr-0.06 C 합금의 재결정거동에 관한 연구
- Yoon, Kook Han (Special Alloy Research Lab., Korea Institute of Science and Technology) ;
-
Lee, Chong Mu
(Department of Metallurgical Engineering, Inha University) ;
- Choi, Ju (Special Alloy Research Lab., Korea Institute of Science and Technology)
- Received : 1992.09.18
- Published : 1992.09.25
Abstract
Plasma are melting method was used in making Mo-1.17 Ti-0.18 Zr-0.06 C ingot having over 99% of the theoretical density. Oxygen content herewith, decreased from the origin of 830ppm to 40ppm. After cold rolling of Mo alloy by 50%, the recrystallization behaviors were studied in the temperature range from
플라즈마 아크 용해법으로 이론밀도비 99% 이상인 Mo-1.17 Ti-0.18 Zr-0.06 C 잉고트를 제조하였다. 이때 산소함량은 초기 830ppm에서 40ppm으로 감소하였다. 열간단조 후, 50% 냉간 압연하여 두께 2mm의 판재를 만들어 시편으로 사용하였다. Mo 합금판재의 재결정거동을 조사하기 위하여