Recrystallization Behavior of Mo-1.17 Ti-0.18 Zr-0.06 C Alloy

Mo-1.17 Ti-0.18 Zr-0.06 C 합금의 재결정거동에 관한 연구

Plasma are melting method was used in making Mo-1.17 Ti-0.18 Zr-0.06 C ingot having over 99% of the theoretical density. Oxygen content herewith, decreased from the origin of 830ppm to 40ppm. After cold rolling of Mo alloy by 50%, the recrystallization behaviors were studied in the temperature range from $800^{\circ}C$ to $2100^{\circ}C$ for 1 hr isochronical holding time and also at $1400^{\circ}C$, $1500^{\circ}C$, $1600^{\circ}C$ for varying isothermal holding time 0 to 108000sec. The complete recrystallization temperature of Mo was $1400^{\circ}C$ but that of Mo alloy was $1700^{\circ}C$. 50%-1 hr recrystallization temperature of Mo alloy sheet was about $1500^{\circ}C$ and when compared to Mo there was an increase of over $300^{\circ}C$. The activation energy of recrystallization of Mo alloy sheet was 508kJ/mol.

플라즈마 아크 용해법으로 이론밀도비 99% 이상인 Mo-1.17 Ti-0.18 Zr-0.06 C 잉고트를 제조하였다. 이때 산소함량은 초기 830ppm에서 40ppm으로 감소하였다. 열간단조 후, 50% 냉간 압연하여 두께 2mm의 판재를 만들어 시편으로 사용하였다. Mo 합금판재의 재결정거동을 조사하기 위하여 $800{\sim}2100^{\circ}C$ 구간에서 1시간 동안 등시열처리하였고, $1400^{\circ}C$, $1500^{\circ}C$, $1600^{\circ}C$에서 0~10800sec 동안 등온열처리하였다. 완전한 재결정은 Mo의 경우 $1400^{\circ}C$에서 종료되었으나 Mo 합금의 경우 $1700^{\circ}C$에서 완료되었다. 또한 Mo 합금의 50%-1시간 재결정온도는 약 $1500^{\circ}C$로서 Mo에 비하여 $300^{\circ}C$ 이상 증가된 것을 알 수 있었다. Mo 합금의 재결정에 필요한 활성화에너지는 508kJ/mol이었다.