The Analysis of Lattice Distortion of $Ba(Zn_{1/3}Ta_{2/3})O_3$ by X-ray Diffraction

X-선 회절분석법에 의한 $Ba(Zn_{1/3}Ta_{2/3})O_3$의 격자 비틀림 측정

  • Kim, Chong-Don (Ceramic Laboratory, korea Institute of Science and Technology) ;
  • Kim, In-Tae (Ceramic Laboratory, korea Institute of Science and Technology) ;
  • Je, Hae-June (Ceramic Laboratory, korea Institute of Science and Technology)
  • 김정돈 (한국과학기술연구원 세라믹스 연구실) ;
  • 김인태 (한국과학기술연구원 세라믹스 연구실) ;
  • 제해준 (한국과학기술연구원 세라믹스 연구실)
  • Received : 1992.03.15
  • Published : 1992.03.25
Download PDF
⟨ Previous Next ⟩

Abstract

Ordering phenomena were observed for Zn and Ta cations of $Ba(Zn_{1/3}Ta_{2/3})O_3$ under particular heat treatments, followed by a considerable lattice distortion. This lattice distortion was measured by X-ray powder diffraction with a precision of higher than 1/10,000. From this investigation, a significant lattice distortion occurred within 30 min. of sintering at $1350^{\circ}C$, and it was increased with sintering time.

$Ba(Zn_{1/3}Ta_{2/3})O_3$는 고온에서 열처리시 Zn과 Ta 이온이 ordering을 일으키며 이때 격자 비틀림이 일어난다. 본 실험에서는 이러한 격자비틀림을 X-선 분말회절법을 사용하여 1/10,000 이상의 정밀도로 측정하였으며, 그 결과 $Ba(Zn_{1/3}Ta_{2/3})O_3$는 $1350^{\circ}C$ 30분 소결시에도 상당한 정도의 격자 비틀림이 발생하며 이러한 격자비틀림은 소결시간이 길어질수록 증가함을 관찰하였다.