HP-GPC Analysis for Characteristics Change of Asphalt Cement Due to Aging

노화(老化)에 의한 아스팔트 시멘트 형질변화(形質變化)의 HP-GPC 분석(分析)

This study was conducted to evaluate physical property change of asphalt cement chromatograms (by HP-GPC) were experimentally obtained from 3 types of AC-20 virgin ACs, 5 and 24-hour artificially aged ACs, and naturally aged 4 ACs that were recovered from 4 different roads. Absolute viscosity, kinematic visoosity and penetration were the physical properties tested. THF was used for mobil phase and RI detector was used as a detector for Hp-GPC testing. Correlation between each physical property change and the chromatogram variation was evaluated. Each chromatogram was divided into ten-equal-time slices. The percentage areas of 10 slices and each physical property were used for statistical correlation evaluation. Statistical analysis results showed that eaoh physical property had a strong correlation with the chromatogram characteristics. Aging was identified as a mechanism of change of molecular size distribution - increasing large size molecules and reducing coresponding samll size molecules.

본 연구(研究)는 노화(老化)에 의한 아스팔트시멘트의 물리적 성질변화를 크로마토그램에 근거(根據)하여 유성학적(流性學的)으로 고찰(考察)하였다. 3종류의 AC-20 아스팔트시멘트와 그것을 인공노화(人工老化)시킨 것 그리고 도로(道路)포장의 코어로부터 추출(抽出)해낸 자연노화(自然老化)된 아스팔트에 대하여 3가지 물리적 성질과, 고압(高壓) 겔 투과(透過) 크로마토그래프(HP-GPC)를 이용한 크로마토그램(분자입도분포(分子粒度分布))을 측정(測定)하였다. 이 물리적 성질과 HP-GPC 결과를 분석(分析)하여 노화전후(老化前後)의 크로마토그램과 물리적 성질의 상관관계(相關關係)를 고찰(考察)하였다. 물리적 성질로는 점도(粘度), 동점도(動粘度), 퇴입도(退入度)를 구하였으며, HP-GPC 시험에서는 THF가 순환용액으로 사용되고 RI 검출기가 사용되었다. 크로마토그램을 같은 시간간격(時間間隔)의 10구간으로 분할(分割)하여, 각 구간의 분할면적비(分割面積比)와 물리적 성질이 통계분석(統計分析)에 사용되었다. 이 연구결과(研究結果) 아스팔트시멘트의 물리적 성질은 크로마토그램 특성과 매우 밀접한 관계가 있음을 알 수 있었다. 또한 아스팔트의 노화는 유성학적으로 분자입도의 구성비가 변환되는 과정임을 알 수 있었다.