Doping Effects with $GeO_{2}$ and $SnO_{2}$ in Mn-Zn Ferrites

Mn-Zn 훼라이트의 $GeO_{2}$와 $SnO_{2}$ 첨가효과

The permeability vs. temperature curve, the loss factor and the microstructure of a commercial Mn-Zn ferrites were investigated by X-ray diffractometer, SEM and LCR meter, where the additives, such as $SnO_{2}$ and $GeO_{2}$, were added to the main composition. Their wt% were 0.05, 0.3 and 1.0, respectively. When the content of additives increased, the SPM (Secondary Peak Maximum) of the permeability moved from $80^{\circ}C$ to below the room temperature. This movement, without the significant change of the microstructure, is because Sn and Ge, having the different ionic radius, were soluble in the matrix. There was no variation of the permeability with the frequency up to 100 kHz. And the loss factor showed the maximum value at 10 kHz.

상용의 Mn-Zn 훼라이트에 $GeO_{2}$와 $SnO_{2}$를 0.05, 0.3, 1.0 wt% 첨가하여 투자율의 온도특성, 손실인자 및 미세구조변화를 X-선 회절분석기, 주사전자현미경 및 LCR meter를 이용하여 관찰 하였다. $SnO_{2}$, $GeO_{2}$의 첨가량이 증가함에 따라, 투자율의 SPM(Secondary Peak Maximum)는 약 $80^{\circ}C$로부터 상온이하로 이동하였다. 미세구조의 현격한 변화없이 수반된 이러한 SPM의 이동은 이온 반경이 다른 Sn과 Ge이 주격자에 고용되었기 때문으로 판단된다. 투자율 및 손실인자의 주파수 의존성은 투자율이 100 kHz까지 모든조성에서 큰 변화가 없음을 알수있었고 손실인자는 10 kHz에서 최대값을 얻을 수 있었다.