Abstract
In a $Co_{67}Fe_{4.5}Nb_{2}Si_{10}B_{15}$ amorphous alloy ribbon the effect to two-step annealing on the soft magnetic properties has been studied. By two-step annealing method which the second annealing at low temperature of $310^{\circ}C$ for 2 hours is undertaken after the primary annealing at high temperature above $480^{\circ}C$ for 20 minutes at the vacuum state, the coercive force and the squareness are not changed nearly but the initial permeability at d.c. and the effective permeability at a.c. are remark-ably increased compared with the one-step annealing. The maxima of the initial permeability and the effective permeability at 1 kHz after the two-step annealing are 290,000 and 41,000, respectively, which are 30% higher than those of the one-step annealing. The change of magnetic properties with annealing temperature is discussed in terms of the residual stress, the domain size, the cluster and the crystalline phase.
$Co_{67}Fe_{4.5}Nb_{2}Si_{10}B_{15}$ 비정질합금리본에서 2단 어닐링이 자기특성에 미치는 영향을 조사 하였다. 고온인 $480^{\circ}C$ 이상에서 20분간 1단 어닐링한 리본을 저온인 $310^{\circ}C$에서 2시간 동안 2단으로 진공어닐링한 결과 보자력과 각형비는 1단 어닐링한 경우와 거의 비슷한 값들을 나타내었으나, 직류 및 교류투자율은 1단 어닐링에 비해 현저히 높아졌다. 2단 어닐링시 직류 및 1 kHz에서의 교류투자율의 최대치는 각각 약 290,000과 41,000으로서 1단 어닐링에 비해 30% 이상 증가하였다. 어닐링온도에 따른 자성의 변화는 3단계로 나누어 내부응력, 자구크기, cluster 및 결정상의 변화를 주요 요인으로 하여 고찰하였다.