Abstract
The optical absorption characteristics of glasses colored by CdS. CdSe, $CdS_{1-x}Se_x$,ZnS, and ZnSe microcrystallites have been studied with emphasis on changes of the cut-off wavelength. The sharpcut filters with various cut-off wavelengths were fabricated by controlling the composition and the heat-treatment temperature. The cut-off wavelength shifts due to the different heat-treatment temperatures for CdS. CdSe, ZnS, and ZnSe doped SK-16 glasses were found to be relatively small(~30 nm). However, by treating the CdS1,Se, doped SK-16 glasses with different x values at the same heattreatment temperature, it was possible to obtain the filters with various cut-off wavelengths(~130 nm) without losing the high extinction coefficients of the filters. The filter glasses with various cut-off wavelngths(~100 nm) and high extinction coefficiencts were also produced by treating the CdSe and $CdS_{0.5}Se_{0.5}$ doped ZK-1 glasses at different temperatures.
본 연구에서는 CdS, CdSe, ZnS, ZnSe 반도체를 첨가한 SK-16 유리와 ZK-1 유리를 직접 제작하고 열처리하여 유리속에 반도체의 미세결정을 생성시켜 착색유리를 만들고 sharp-cut용 광학 filter로써의 특성을 조사하였다. CdS, CdSe, ZnS 및 ZnSe 반도체를 첨가한 SK-16유리는 열처리돈도를 달리하였을 경우 광흡수단을 변화시킬 수 있는 범위가 30nm정도로 아주 좁았다. 그러나 $CdS_{1-x}Se_x$를 첨가한 SK-16 유리는 x값을 변화시키면서 열처리 함으로써 광흡수단을 ~130nm범위에서 변화시킬 수 있었고 광흡수계수도 높아 sharp-cut용 광학 filter용으로 좋은 특성을 나타내었다. CdSe와 $CdS_{0.5}Se_{0.5}$ 반도체를 첨가한 ZK-1 유리는 열처리온도를 달리 함으로서 흡수단을 변화시킬 수 있는 범위가 ~100nm나 되고 광흡수게수도 아주 높아 sharp-cut용 광학 fiter로 아주 우수한 특성을 나타내었다.