The Study of the Dielectric and Piezoeletric Properties of 0.05Pb(AlS12/3TWS11/3T)OS13T-0.95Pb(ZrS10.52TTiS10.48T)OS13T System Modified with MnOS12T and FeS12TOS13T

MnO2, Fe2O3 첨가에 따른 0.05Pb(Al2/3W1/3)O3-0.95Pb(Zr0.52Ti0.48)O3계의 유전 및 압전 특성에 관한 연구

In this study, dielectric and piezoelectric properties of 0.05Pb(AlS12/3TWS11/3T)OS13T-0.95Pb(ZrS10.52TTiS10.48T)OS13T system ceramics were investigated with respect to the variations of MnOS12T and FeS12TOS13T additions amounts. The results obtained in this study are summarized as follows: 1. As the amounts of MnOS12T and FeS12TOS13T are increased, tetragonality(c/a) and apparent density were decreased but grain size was increased, also the limits of solubility were revealed because pores were formed at the amounts of 0.3wt% MnOS12T and 0.5wt% FeS12TOS13T. 2. AS the increasing of amounts of MnOS12T and FeS12TOS13T, the temperature of phase transition(TS1cT) was decreased, and pemeability had maximum value at the amount of 0.3wt% MnOS12T but were sharply decreasd for the increasing FeS12TOS13T amounts. 3. As the amounts of MnOS12T and FeS12TOS13T are increased, the electro-mechanical coupling factor(kS1pT) was decreased from 60% to 41%, 19% respectively, but mechanical quality factor(QS1mT) had maximum values 720 for amount of 0.3wt% MnOS12T and 320 the amount of 0.5wt% FeS12TOS13T.