Effect of Metal Oxide Additives on Hydrogen Production in the Steam-Iron Process

철-수증기 반응에 의한 수소생성에 미치는 금속산화물의 첨가효과

  • Lee, Dae-Haeng (Department of Chemical Technology, Chonnam National University) ;
  • Moon, Hee (Department of Chemical Technology, Chonnam National University) ;
  • Park, Heung-Chul (Department of Chemical Technology, Chonnam National University)
  • 이대행 (전남대학교 공과대학 공업화학과) ;
  • 문희 (전남대학교 공과대학 공업화학과) ;
  • 박흥철 (전남대학교 공과대학 공업화학과)
  • Received : 1990.10.08
  • Published : 1991.03.25

Abstract

The production of hydrogen from steam by reduced iron with additives such as CuO, $In_2O_3$, $MoO_3$ and $WO_3$ has been kinetically investigated. It was shown that all additives have a promoting effect on reaction activity in the order of $$MoO_3{\gg}In_2O_3{\sim_=}WO_3{\sim_=}CuO$$. The shrinking core model was applied to predict the complete conversion time and the results were quite comparable with experimental values. The reaction was carried out in a fixed flow reactor packed with reduced iron with 1 wt % of additives under the conditions, $600-750^{\circ}C$, Ar flow rate of 1 L/min and steam partial pressure of 0.085 atm. The apparent activation energies were 14.2, 20.9, 21.3, 22.4 and 27.9 kJ/mol with $MoO_3$, $In_2O_3$, $WO_3$, CuO and without additive, respectively.

금속산화물 CuO, $In_2O_3$, $MoO_3$, $WO_3$을 첨가시킨 환원철에 의한 수증기로부터 수소생성을 반응속도론적 관점에서 조사하였다. 첨가제는 수소생성에 대한 활성증진효과를 나타내었으며, 크기의 순서는 $$MoO_3{\gg}In_2O_3{\sim_=}WO_3{\sim_=}CuO$$이었다. 속도해석에서 반응완료시간을 예측하기 위하여 수축 핵 모델(Shrinking Core Model)을 적용한 추산결과는 실험치와 대체로 잘 일치하였다. 상압 유동식 반응장치를 이용하여 $600-750^{\circ}C$의 온도와 첨가제의 양 l wt %, Ar 유량 1 L/min, 수증기분압 0.085 atm에서 얻어진 겉보기 활성화에너지는 환원철 단독의 경우 27.9kJ/mol, 첨가제 $MoO_3$는 14.2, $In_2O_3$는 20.9, $WO_3$은 21.3, CuO는 22.4 kJ/mol을 각각 나타내었다.