초록
The purpose of this study was to observe in vitro chloride corrosion behavior from 5 kinds of amalgam (Caulk spheracal, Amalcap, Dispersalloy, Tytin, Sybralloy) as a function of time after tritruration by using potentiostat. After each amalgam alloy and Hg was triturated as the direction of the manufacturer by the mechanical amalgamator, the triturated mass was inserted the cyrindrical matal mold ($12{\times}10mm$) and was condensed by using routine manner. The specimen was removed from the mold and was stored at room temperature for 1 week, 1 month and 3 months, and standard surface preparation was routine carried out. The 0.9% saline solution was used as electrolyte in pH 6.8~7.0 at $30{\pm}0.5.^{\circ}C$. The open circuit potential was determined after 30 minutes' immersion of 1 week, 1 month and 3 month old specimens. The scan rate was 1 mV/sec and the surface area of amalgam exposed to the solution was $0.65\;Cm^2$ for each specimen. All potentials reported are with respect to a silver / silver chloride electrode (SSE). The following result was obtained. 1. All amalgam specimens became more noble corrosion potentials which represent the improved corrosion resistance as the time elapsed. 2. Three kinds of high copper amalgam always exhibited more noble potential than low copper amalgam at 1 week, 1 month and 3 months. 3. Two kinds of low copper amalgam had the similar polarization curve pattern with 3 current peaks at each time period and current densities associated with these peaks were decreased as aging especially in caulk spherical amalgam. 4. All kinds of high copper amalgam had the similar polarization curve pattern with absence of prominent current peak at each time period, but the polarization curve of D amalgam had one apparent current peak at 1 week.