Effect of Thermal Cycling on Shape Memory Effect and Stabilization of Parent Phase in Fe-21%Mn Alloy

Fe-21%Mn 합금의 형상기억효과와 모상의 안정화에 미치는 반복열처리의 영향

Effect of thermal cycling on shape memory effect and stabilization of austenite was investigated in Fe-21%Mn alloy. The thermal cyclic treatment was carried out with two types, room temperature${\leftrightarrow}215^{\circ}C$ and room temperature${\leftrightarrow}260^{\circ}C$. In case of the room temperature${\leftrightarrow}215^{\circ}C$, the SME was rapidly increased up to 3 cycles and maintained nearly constant value regardless of further cycles. In case of the room temperature${\leftrightarrow}260^{\circ}C$, however, the SME was increased with increasing the thermal cycle up to 5 cycles and decreased gradually with further cycle. The variation of the ${\varepsilon}$ martensite volume pet with the thermal cycle was in good agreement with the variation of the SME. Therefore, the change of the SME due to the cyclic treatment was explained with the change of the ${\varepsilon}$ martensite content. As the thermal cycle was increased, the $M_s$ temperature was decreased, and the $A_s$ and $A_f$ temperatures were increased, respectively.