A Study on the Pore Characteristics of the U$O_2$ Fuel

U$O_2$핵연료의 기공 특성에 대한 연구

  • Song, K-W (Korea Atomic Energy Research Institute) ;
  • K.S. Seo (Korea Atomic Energy Research Institute) ;
  • Sohn, D-S (Korea Atomic Energy Research Institute) ;
  • Kim, S.H. (Korea Atomic Energy Research Institute) ;
  • I.S.Chang (Korea Atomic Energy Research Institute) ;
  • H.S. Chang (Korea Nuclear Fuel Company)
  • Published : 1991.03.01
Download PDF
⟨ Previous Next ⟩

Abstract

The microstructure and pore characteristics have been studied on the sintered UO$_2$pellet which was made of the UO$_2$powder manufactured via AUC process. The open porosity decrease with the density and is nearly annihilated above the density of 10.45 g/㎤. The round pore smaller than 3 $\mu$m exist In all densities. The large and elongated pore appears additionally In low density The pore in low density is more elongated than the pore in high density The distribution of the pore area versus the pore size is monomodal and shows its peak on the pore size of 2 to 3 $\mu$m. As the density decreases, the related area of large pore Increases.

AUC공정으로 제조된 $UO_2$분말을 사용하여 소결체를 제조하여 미세 조직과 기공특성에 대하여 시험하였다. 개기공은 소결밀도 증가에 따라서 감소하였으며, 소결밀도 10.45 g/㎤ 이상에서는 거의 소멸하였다. 3$\mu$m보다 작은 크기의 둥근 기공이 모든 밀도에서 나타났고 낮은 밀도에서는 이것외에도 긴 기공이 관찰되었다. 같은 크기의 기공일지라도 밀도가 낮아지면 기공이 더욱 길게 나타났다. 기공크기에 따른 기공 면적의 분포는 mono 모우드이고, 2~3$\mu$m 기공크기에서 최대치를 보이는 분포를 보였다. 또한 밀도가 감소할수록 큰 기공에 관련된 면적이 증가하였다.