초록
The effect of thermal cycling on the hydrogenation characteristics of the $Mg_2Cu-H$ system was investigated in order to study of intrinsic degradation of the system. The hydrogen storage capacity decreased with thermal cycling from $573^{\circ}K$ to $663^{\circ}K$. By the thermal analysis it is found that stable $MgH_2$ hydride is formed during thermal cycling. With a heat treatment at $693^{\circ}K$ at a hydrogen pressure of 16 atm, the hydrogenation rate drastically decreased. From these observation, it suggested that the intrinsic degradation of $Mg_2Cu$ system results from mainly the formation of stable $MgH_2$ hydride phase.