유기물 바인더를 사용한 $YBa_2Cu_3O_{7-{\delta}}$ 초전도 Coil의 제조

Fabrication of $YBa_2Cu_3O_{7-{\delta}}$ Superconducting Coils with Polymer Binder

  • 발행 : 1990.03.01

초록

One of the possible ways to make a flexible wire of high-Tc superconductiong ceramics is the extrusion of a mixture slurry of superconducting powder with an appropriate polymer binder. The fabrication procedure for $YBa_2Cu_3O_{7-{\delta}}$ superconducting coils with this plastic mass is described. The major factors limiting the formation of extruded wire are the binder content, powder size, and entrapped gas in the mixture slurries. The optimum content of binder for both good flexbility and strength of wire was estimated to be 30wt%. The finer the powder size is, the more homogeneous structure the extruded wire has. The vacuum degassing before extrusion was necessary to remove the entrapped gas in as-extruded wire. The formability of wire depends greatly on the wire radius and binder content. After burning out the binder and the successive sintering, the contacts between the superconducting grains could be made. The resistivity vs. temperature behavior measured in the final wire showed the transition temperature of 90K with narrow transition width. However, the critical current densities of these wires are much lower in comparison to those of conventional bulk specimens.

키워드

참고문헌

  1. Z. Phys. v.B64 Possible High Tc Superconductivity in the Ba-La-Cu-O System J.C. Bednorz;K.A. Muller
  2. Phys. Rev. Lett. v.58 Superconductivity at 93K in a New Mixed Phase Y-Ba-Cu-O Compound System at Ambient Pressure M.K. Wu;J.R. Ashburn;C.J. Torng;P.H. Hor;R.L. Menz;L. Gao;Z. Huang;Y.Q. Wang;C.W. Chu
  3. Science v.241 Processing Techniques for the 93K Superconductor Ba₂YCu₃$O_{7-δ}$ D.W. Murphy;D.W. Johnson, Jr.;S. Jin;R.E. Howard
  4. Phys. Rev. v.B27 Melt-Textured Growth of Polycrystalline YBa₂Cu₃$O_{7-δ}$ with High Transport Jc at 77K S. Jin;T.H. Tiefel;R.C. Sherwood;R.B. Van Dover;M.E. Davis;G.W. Kammlott;R.A. Fastnacht
  5. Supercond. Sci. Technol. v.1 The Fabrication of Ceramic Superconducting Wire M.A. Lusk;J.A. Lund;A.C.D. Chakladert;M. Burbank;A.A. Fife;S. Lee;B. Taylor;J. Vrba
  6. Paper Presented at the World Congress on Superconductivity Fabrication of Bulk Superconducting Ceramics K.C. Goretta;J.Y. Dusek;J.P. Singh;M.T. Lanagan;U. Balachandran;S.E. Dorris;R.B. Poeppel
  7. Chemisty of High Temperature Superconductors Fabrication of YBa₂Cu₃$O_{7-δ}$ Superconducting Ceramics R.B. Poeppel;B.K. Flandermeyer;J.T. Dusek;I.D. Bloom
  8. J. Mater. Sci. Lett. v.5 Critical Current Density in Tape-Cast YBa₂Cu₃$O_{7-δ}$ Superconductors G.J.J. Beckers;R.A. Terpstra
  9. Instruction Sheet for Claden Ceramic Binder Cerbind 73140 Claden Technology Inc.
  10. Appl. Phys. Lett. v.51 Preparation of Single Crystals of Superconducting YBa₂Cu₃$O_{7-δ}$ form CuO Melts M.A. Damento;K.A. Gischmeidner, Jr.;R.W. McCallum
  11. J. Crystal Growth v.85 On the Defect Structure of Grain Boundaries in Ba₂YCu₃$O_{7-δ}$ S. Nakahara;G.J. Fisanick;M.F. Yan;R.B. van Dover;T. Boone