투명 결정화유리의 구조에 관한 연구

Studies on the Structure of Transparent Glass Ceramics

  • 발행 : 1990.02.01

초록

Parent glasses for the experiments were prepared to be ratio of Li2O : Al2O3 : SiO2=4.5 : 25 : 70.5 as basic components, and TiO2 and ZrO2 in the mixing ratio of 1 : 1 were added as the nucleating agents, whose contents were increased in each sample. DTA, XRD, SEM, IR were observed, and thermal expansion and transmissivities were measured for the crystallized samples under the controlled heat-treatments. The transformation temperatures and the dilatometric softening temperatures in thermal expansion curves, and also the exothermic peaks in differential thermo-analytical curves were shifted to lower temperature. The crystal phase deposited through the heat-treatment was identified as ${\beta}$-quartz solid solution with XRD and IR analysis. The crystalline phases in oopactified samples were ${\beta}$-spodumene coexiting with ${\beta}$-quartz solid solution. The samples having more than 3% nucleating agents were transparent. The crystallized grain sizes were ranged 0.05 to 0.1$\mu\textrm{m}$. The crystallized transparent samples were exceeded 85% in the transmissivity.

키워드

참고문헌

  1. British Patent 752243 S.D. Stookey
  2. Phil. Mag. v.41 no.4 On the Light from the Sky, its Polarisation and Colour L. Rayleigh;J.W. Strut
  3. Ann Physik v.25 Beitrage Zur Optik Truber Medien, Speziell Kolloidaller Metallosunger G.Mie
  4. J. Mat. Sci. v.4 Transparent Glass-Ceramics G.H. Beall;D.A. Duke
  5. J. Am. Ceram. Soc. v.61 no.5 Microstructure and Kinetics of Crystallization of MgO-Al₂O₃-SiO₂ Glass-Ceramics W.A. Zdaniewski
  6. United States Patent 3241985 S. Kuwayama
  7. J. Am. Ceram. Soc. v.41 no.4 Determination of Percent Crystallinity of Partly Devitrified Glass by X-ray Diffraction S.M. Ohlberg;D.W. Strickler
  8. Glastech, Ber. v.60 no.7 Nucleation in a Precursor Glass for a Li₂O-Al₂O₃-SiO₂ Glass-Ceramics U. Schiffner;W. Pannhorst
  9. Glass Ceramics P.W. McMillan
  10. Anal. Chem. v.39 no.11 Reaction Kinetics in Differential Thermal Analysis H.E. Kissinger
  11. J. Res. Nat. Bur. Stand. v.57 H.E. Kissinger
  12. J. Ceram. Ass. Japan v.76 no.9 Structural Change during the Process of Formation of a Transparent Glass Ceramics Y. Moriya
  13. Glastech v.23 no.5 Microstructure and Crystallization behaviour of a Transparent Glass Ceramics Doped with Fe₂O₃ M.L. Wang;R. Stevens;P. Knott
  14. J. Am. Ceram. Soc. v.57 no.7 Thermal Expansion of Beta Eucryptite H. Schulz