Abstract
The mullite-15v/o ZrO2 composites were prepared by dispersing ZrO2-3m/o Y2O3 powders into the mullite matrix in order to improve the mechanical properties of the mullite. The densification and retention of t-ZrO2 in the matrix of synthetic mullite were also investigated. From IR spectroscopic analysis, the obtained amorphous SiO2-Al2O3 powder was observed to have Si-O-Al chemical bond in its structure which might result in the homogeneous mullite composition. The lattice parameter of the mullite powder calcined above 130$0^{\circ}C$ (a0=7.5468$\AA$) is nearly close to the value of stoichiometric mullite (71.8wt% Al2O3, a0=7.5456$\AA$). The sintering behavior, microstructure, flexural strength and fracture toughness of the mullite and mullite-15v/o ZrO2 composites have been studied. The mullite-15v/o ZrO2(+3m/o Y2O3) ceramics with relative densities of 96% were obtained when sintered at 1$600^{\circ}C$. The flexural strength and fractrue toughness of the composites sintered at 1$600^{\circ}C$(calcination temperature of mullite powders ; 125$0^{\circ}C$) had maximum values of 307MPa and 2.50MPa.m1/2, respectively. The fracture toughness improvement in the mullite-ZrO2 cmoposite is assumed to be resulted from the combined effect of the stress-induced phase transformation of tetragonal ZrO2 and the crack deflection due to microcracking by the monoclinic ZrO2 formation.