Optical Properties of $Bi_2S_3$ Thin films

$Bi_2S_3$ 薄膜의 光學的 特性

$Bi_2S_3$ polycrystalline and $Bi_2S_3$ amorphous thin tilm were grown by the evaporation method. The measured lattic parameters were $a=1.708{\AA},\;b=0.351{\AA},\;and\;C=3.943{\AA}$ at substrate temperature $210^{cric}C$ were shown to have the orthorhombic structure. The energy gape of $Bi_2S_3$ polycrystalline that was made from thin film were measured to be 1.375eV at $289^{cric}K.$ The optical band gap of $Bi_2S_3$ amorphous thin film was measured to be 1.71eV at $289^{cric}K.$ It was supposed to mechanism that a photon absorption was changed at the center of 674nm (1.84eV)

$Bi_2S_3$다결정과 $Bi_2S_3$ 무정형 박막은 증착방법에 의해서 성장되었다. 측정된 격자상수들은 기판온도 $210^{circ}C$에서 $a=1.708{\AA},\;b=3.943{\AA} 그리고 $c=3.943{\AA}$이었으며, orthorhombic 구조를 가진것으로 나타내었다. 다결정 박막 $Bi_2S_3$energy은 $289^{circ}C$ 에서 1.375eV로 측정되었다. 674nm의 중심에서는 변화된 광자흡수 구조로 생각되어졌다.