Deterioration of Polyethylene Films Induced by Partial Discharge and Variations Observed in Mechanical Properties
Polyethylene film의 부분방전열화와 역학적 특성
Abstract
Deterioration induced by partial discharge was investigated for low-density polyethylene samples. Under an electrical field, a cold-drawn PE film was stretched perpendicularly to the direction of the original drawing. The starting voltage of the discharge shows a minimum at the draw ratio of 1.2 to 1.8. Around the same draw ratio, the elastic modulus and mechanical loss factor (tan S) of the sample exhibit a minimum and a maximum, respectively. According to the X-ray analysis, the size itf microcrystals decreases with increasing draw ratios. Reorientation of the ru01ecular chains was observed above a draw ratio of 1.5 by the IR method.
低密度 Polyethylene film을 冷延伸된 方向에 對해서 直勇方向으로 延伸하면, 延伸比 1.2~1.8 付近에서 部分放電에 의한 劣化가 顯著히 增加하고, Void發生에 의한 部分放電 開始電壓이 低下한다. 延伸 film에 對해 强制振動法에 의해 求한 彈性率 및 力學的 tan
Keywords