Abstract
Ion-exchange porous glasses were prepared by heat treatment and subsequently hydro thermalor acid leaching treatment $10Li_2O$.$(90-x)B_2O_3$.$xSiO_2$ base glasses containing various amount of $Al_2O_3$ or $MoO_3$. It was investigated how the phase separation and the cation exchange capacity(CEC) were affected by the addition of $Al_2O_3$ or $MoO_3$. The optimum condition of phase separation in these glasses was about 48$0^{\circ}C$ for 10 hrs. The degree of phase separation was rapidly suppressed by the addition of $Al_2O_3$ up to 10 mol% and thereafter suppression effect was decreased. The maximum value of CEC, about 252meq/100g, was observed with the $1OLi_2O$.$45B_2O_3$.$45SiO_2+7.5Al_2O_3$ porous glass prepared by hydrothermal treatment and its mean pore radius was about 16.3A. The addition of $MoO_3$ accelerated phase separation and leaching rate. Looking at the remakable increment of pore diameter and pore volume of these porous glasses by the addition of $MoO_3$, the effect of $MoO_3$ may be ascribed to the lowering of silica concentration in the borate phase and to the forming of water-soluble complex with silica during the leaching treatment.
$10Li_2O$.$(90-x)B_2O_3$.$xSiO_2$ 기초유리에 $Al_2O_3$ 또는 $MoO_3$를 첨가한 유리를 열처리한 후 열수 또는 산처리하여 이온교환성 다공질 유리를 제조하였다. 그리고 $Al_2O_3$ 또는 $MoO_3$ 첨가가 분상과 양이온교환능(CEC)에 미치는 영향을 조사하였다. 이들 유리의 분상최적조건은 48$0^{\circ}C$, 10시간 열처리하였다. 분상은 $Al_2O_3$ 10mol%까지는 급격히 억제되고 그 이후에는 분상억제 효과가 완화되었다. 양이온교환능의 최대값은 $1OLi_2O$.$45B_2O_3$.$45SiO_2+7.5Al_2O_3$ 조성유리를 열수처리한 다공질유리에서 약 252meq/100g을 나타냈으며 이 유리의 세공평균반경은 약 16.3A이었다. $MoO_3$ 첨가는 분상과 용출속도를 증가시켰다. $MoO_3$첨가에 의해 다공질유리의 세공반경과 세공용적이 크게 증가하는 것으로 보아 $MoO_3$는 유리의 붕산염상중의 실리카 농도를 낮추고 용출처리중 실리카를 수용성 착체로 형성시키는 효과가 있다고 생각된다.