Experimental Study on the Properties of Strength of the No-Fines Concrete

No-Fines Concrete의 강도특성(强度特性)에 관(關)한 실험적(實驗的) 연구(硏究)

No-fines concrete is concrete from which the fine aggregate fraction has been omitted. The concrete so formed, consisting only of coarse aggregate, cement, and water, has large voids uniformly distributed through its mass. This study was performed to obtain the basic data which can be applied to the use of no-fines concrete. The data was based on the properties of no-fines concrete depending upon various mixing ratios. The results obtained were summarized as follows. 1. Test result of the consistency, suitable water-cement ratio was increased with the increasing of mixing ratio. 2. At the suitable water-cement ratio, the highest strengths were showed. But it gradually was decreased with the increasing of mixing ratio and strengths are considerably lower than that of conventional portland cement concrete. 3. The relations between compressive and tensile strength were highly singnificant as a straight line shaped. The strength ratio was decreased with the increasing of mixing ratio and considerably lower than of conventional portland cement concrete. 4. Bulk density was decreased with the increasing of the mixing ratio, and was similar to that of the conventional portland cement concrete at mixing ratio 1:4. 5. The relations between strength and bulk density were highly significant as a straight line shaped. The decreasing ratio of strengths was higher than that of bulk density.

이 연구(硏究)는 no-fines concrete의 배합비(配合比)와 물-시멘트비(比)에 따른 강도특성(强度特性)을 구명(究明)함으로써, 이의 효과적(效果的)인 사용(使用)을 위한 기초적(基礎的)인 자료(資料)를 마련하는데 있으며, 이 연구(硏究)에서 얻어진 결과(結果)를 요약(要約)하면 다음과 같다. 1. Consistency의 적정(滴定)한 물-시멘트비(比)는 시멘트와 조골재(粗骨材)의 배합비(配合比)가 클수록 증가(增加)하는 경향(傾向)을 보였다. 2. 압축(壓縮)과 인장강도(引張强度)는 각(各) 배합비별(配合比別) consistency의 적합(適合)한 물-시멘트비(比)에서 최대강도(最大强度)가 나타났고, 보통(普通)시멘트 콘크리트에 비(比)하여 1:4 배합(配合)에서는 비슷한 강도(强度)를 나타내었으나 배합비(配合比)가 증가(增加) 할수록 강도(强度)가 현저히 저하(低下)하는 경향(傾向)을 보였다. 3. 압축(壓縮)과 인장강도(引張强度)와의 상관관계(相關關係)는 직선형(直線形)으로서 고도(高度)의 유의성(有意性)이 있었으며 이들의 강도비(强度比)는 재령(材齡)이 증가(增加) 할수록 증가(增加)하였고, 배합비(配合比)가 클수록 감소(減少)하였으며, 보통(普通)시멘트 콘크리트보다는 작게 나타났다. 4. 밀도(密度)는 배합비(配合比)가 증가(增加) 할수록 감소(減少)하는 경향(傾向)을 보였으며, 보통(普通)시멘트 콘크리트에 비(比)하여 배합비(配合比) 1:4에서는 근사(近似)한 값을 나타내었으나 배합비(配合比)가 증가(增加) 할수록 감소(減少)하는 경향(傾向)을 보였다. 5. 강도(强度)와 밀도(密度)와의 상관관계(相關關係)는 직선형(直線形)으로서 고도(高度)의 유의성(有意性)이 인정(認定)되었고, 밀도(密度)의 감소율(減少率)보다는 강도(强度)의 감소율(減少率)이 더 크게 나타나는 경향(傾向)을 보였다.