A Study on the Shear Behavior of Reinforced Concrete Structures

철근(鐵筋)콘크리트 구조물(構造物)의 전단거동(剪斷擧動)에 관한 연구(研究)

Fatigue fracture of reinforced concrete structures are characterized by considerably larger strains and microcracking as compared to fracture of R.C. structures under static loading. The strain of stirrup is increased suddenly by the occuring of inclined crack and the average strain ${\epsilon}_{\omega}$ of all stirrups in a structure at maximum load increase approximately in proportion to log N. The structures critical in longitudinal reinforcement seemed to have an endurance limit of 60~70 percent of static ultimate strengths for 1,000,000 cycles. In this test, the average fatigue strength at 1,000,000 cycles for all structures tested was approximately 65 percent of the static ultimate strength.

피로하중(疲勞荷重)을 받는 RC 구조물은 정하중(靜荷重)을 받는 경우에 비(比)하여 큰 변형율(變形率)과 미세균열(微細龜裂)을 수반하게 된다. 계속되는 반복하중(反復荷重)으로 인하여 균열(龜裂)은 진전(進展)하게 되고 이러한 균열부(龜裂部)의 응력집중(應力集中)은 스터럽과 인장철근(引張鐵筋)의 변형율(變形率)을 계속 증가(增加)시키게 되어 결과적(結果的)으로 RC 구조물은 파괴(破壞)단계에 이르게 된다. 스터럽의 변형율(變形率)은 사인장균열(斜引張龜裂)이 발생(發生)하면서 급격한 증가(增加)를 보이게 되며 이와 같은 스터럽의 평균변형율(平均變形率)은 반복회수(反復回數)(N)의 증가(增加)에 따라 logN에 비례함을 알 수 있었다. 이와 같이 RC 구조물의 파괴(破壞)는 콘크리트의 균열성장(龜裂成長)과 밀접한 관계가 있다. 또한, RC 구조물의 피로수명(疲勞壽命)을 100만(萬) cycle로서 볼 때 이에 대한 피로강도(疲勞强度)는 정적극한강도(靜的極限强度)의 약 60~70% 정도로 알려져 있다. 본(本) 실험(實驗)에서 사용(使用)된 RC 구조물의 피로강도(疲勞强度)는 약 70%로서 기존의 연구결과(硏究結果)와 잘 부합됨을 확인 할 수 있었다. 따라서 RC 구조물이 이보다 높은 피로하중(疲勞荷重)을 받게되면 피로수명(疲勞壽命)은 훨씬 짧아지게 되며, 이와 같이 피로하중(疲勞荷重)과 피로수명(疲勞壽命)과의 관계는 서로 반비례(反比例)함을 확인할 수 있었다.