Abstract
This study was performed to obtain the basic data which can be applied to the use of foamed mortars using foaming agent of prefoamed type. The data was based on the properties of foamed mortars depending upon various mixing ratios of cement to fine aggregates, flow values and foam-cement ratio to compare those of cement mortar. The results obtained were summarized as follow; 1. At the mixing ratio of 1:0 and the foam-cement ratio of 6.00%, the increasing rate of water-cement ratio was 25% by flow $200{\pm}5mm$, 28% by flow $240{\pm}5mm$ and 32% by flow $280{\pm}5mm$. But it decreased as the mixing ratio gets poorer. The result showed that water amount increased because of the high viscosity caused by the increase of foam-cement ratio. The decrease of water-cement ratio was the greatest when the foam-cement ratio was 1.50%. 2. Absolute aridity bulk density of foamed mortars decreased with the increase of foam-cement ratio and the decrease of flow values. 3. Generally, compressive, tensile and bending strenghs of foamed mortars decreased with the decrease of flow values and the increase of foam-cement ratio. 4. The compressive strength was in proportion to tensile strength. It was estimated that the compressive strength was 8.8 times of tensile strength. The compressive strength was in proportion to bending strength. It was estimated that the compressive strength was 4.0 times of bending strength. The bending strength was in proportion to tensile strength. It was estimated that the bending strength was 2.1 times of tensile strength. 5. At the mixing ratio of 1:1 the lowest absorption rates were showed by foamed mortars, respectively. It was significantly higher at the early stage of immersed water.
본(本) 연구(硏究)는 기포(氣泡)모르터의 특성(特性)을 보통(普通)시멘트 모르터와 비교(比較)함으로써 기포(氣泡)모르터의 합리적(合理的)인 이용(利用)을 위(爲)한 기초자료(基礎資料)를 마련할 목적(目的)으로 전기포주입형(前氣泡注入型)의 기포제(氣泡劑)를 사용(使用)하여 Flow치(値)($200{\pm}5mm$, $240{\pm}5mm$, $280{\pm}5mm$), 기포(氣泡)-시멘트비(比)(0.00%, 0.75%, 1.50%, 3.00%, 4.50%, 6.00%) 및 배합비(配合比) (1 : 0, 1 : 1, 1 : 2, 1 : 3)를 변화(變化)시켜 물-시멘트비(比), 밀도(密度), 제강도(諸强度) 및 흡수율시험(吸水率試驗)을 실시(實施)하였으며, 그 결과(結果)를 요약(要約)하면 다음과 같다. 1. 물-시멘트비(比) 증가율(增加率)은 보통(普通)시멘트 모르터에 비(比)하여 배합비(配合比) 1:0에서 Flow 치(値) $200{\pm}5mm$, $240{\pm}5mm$ 및 $280{\pm}5mm$와 기포(氣泡)-시멘트비(比)가 6.00%일 때 25%, 28% 및 32%로 가장 크게 증가(增加)되었으며 이보다 부배합(負配合)일수록 물-시멘트비(比) 증가율(增加率)은 작게 나타났다. 이와 같은 결과(結果)는 기포(氣泡)-시멘트비(比)가 일정량(一定量) 증가(增加)되면 결성(結性)이 높아져 수량(水量)이 증가(增加)되는 것으로 생각된다. 또한 물-시멘트비(比) 감소율(減少率)은 보통(普通)시멘트 모르터에 비교(比較)하여 기포(氣泡)시멘트비(比)가 1.50% 일 때 각(各) 배합(配合)에서 가장 크게 나타났다. 2. 총건밀도(總乾密度)는 보통(普通)시멘트 모르터에 비(比)하여 기포(氣泡)-시멘트비(比)가 증가(增加)되고 대체로 Flow치(値)가 작을수록 감소현상(減少現象)을 나타냈다. 3. 일반적(一般的)으로 기포(氣泡)모르터의 압축(壓縮), 인장(引張) 및 휨 강도(强度)는 Flow치(値)가 작고 기포(氣泡)-시멘트비(比)가 증가(增加)할수록 감소현상(減少現象)을 보였다. 4. 압축강도(壓縮强度)와 인장강도(引張强度)의 관계(關係)는 직선관계(直線關係)를 나타내며 압축강도(壓縮强度)는 인장강도(引張强度)의 약(約) 8.8배(倍)로 추정(推定)되었다. 압축강도(壓縮强度)와 휨 강도(强度)의 관계(關係)는 직선관계(直線關係)를 나타내며, 압축강도(壓縮强度)는 휨 강도(强度)의 약(約) 4.1배(倍)로 추정(推定)되었다. 휨 강도(强度)와 인장강도(引張强度)의 관계(關係)는 직선관계(直線關係)를 나타내며, 휨 강도(强度)는 인장강도(引張强度)의 약(約)2.1배(倍)로 추정(推定)되었다. 5. 흡수율(吸水率)은 모든 기포(氣泡)모르터에서 배합비(配合比) 1 : 1일 때 가장 낮게 나타났고 이보다 빈배합(貧配合)이며 기포(氣泡)-시멘트비(比)가 증가(增加)할수록 높게 나타났다. 또한 Flow치(値) $240{\pm}5mm$에서 적은 흡수율(吸水率)을 보였다. 그리고, 수침초기(水浸初期)에 기포(氣泡)모르터는 높은 흡수율(吸水率)을 나타냈다.