Studies on Electrostatic Propensity of Fabrics

직물대전성에 관한 연구

This studies has been carried out how to effect on electrostafic propensity of synthetic fabrics by coating with 0.5% acrylic polymer solution which was previously developed by the author to improve anticrease nature of silk. The work conditions are: (A) Applied synthetic polymer was acrylic polymer 525, developed by the author. (B) Electrostatic voltage for various fabrics were carried out by Korea standard abrasion partner with Korea standard (KS K 0905) cotton, nylon, polyester and the self sample fabric. (C) Applied fabrics for the investigations were carried out by using abrasion partner with Korea standard (KS K 0905) cotton, nylon, polyester and the self sample fabric. (D) Electrostatic propensity investigations were carried out by use of sample as silk, nylon, polyester and acrylic fabrics, seperating before finish or after finish. (E) Washing after the finish or the original fabric was carried out by Korea standard method, KS K 0465. Through the investigations, he happened to find many interesting matters and the obtained results are as followings. 1. Electrostatic voltage for the finished fabrics increased more than their original silk, nylon, acrylic fabrics except polyester fabric. (See Table 5) 2. Electrostatic voltage for the finished polyester against K.S. polyester decreased remarkably than the original fabric test. 3. In spite of no problem on electrostatic propensity of silk, it showed high electrostatic voltage between the same nature fabric abrasion, because silk is very weak against abrasion and because the test method had been developed to be useful for only synthetic fabrics. 4. Electrostatic voltage increased more in case of abrasion between different nature of fabrics than the same nature of fabrics. 5. Electrostatic voltage of each fabric increased by repeat of wash. 6. Many investigation data were followed with Contact Electrification Series Principle, another word, the farther each other located fabric on the series abrasion was, the higher electrostatic voltage. (See Fig. 6) 7. Such investigation gives warning of use on the mix fiber spinning service as far as concern with electrification. 8. It may also call attention for such increase of electrification in case any finishing of silk textile.

최근 필자가 견직물방추 가공하기 위해 개발한 acryl 합성수지를 합성섬유와 견직물가공된 것이 정전기발생에 어떠한 영향을 미치는가를 알기 위해 실행했다. 본 실험조건은 다음과 같다. (A) 사용가공처리제는 0.5% acryl polymer 525였다(자가제). (B) 각 직물에 대한 정전기 대전압은 K.S. 규격마찰 검사(KS K 0555) 방식에 따라 했다. (C) 마찰대상 직물로서는 K.S. 표준규격 KS K 0905 cotton, nylon, polyester와 공시직물로 했다. (D) 시료로서 silk, nylon, polyester 및 acryl 직물을 상기 합성수지 가공한 것과 안한 것을 구분해서 정전기 대전압을 조사했다. (E) 가공한 것과 가공하지 않은 시료별로 K.S. 표준규격(KS K 0465) 방식에 의해 세탁했다. 이와 같은 조사로 인하여 여러 가지 흥미있는 결과를 얻었는데 그 결과는 다음과 같다. 1. polyster를 제외하고는 silk, bylon, acryl 직물의 가공직물의 대전압이 가공하지 않은 것의 대전압보다 높았다(Table 5참조). 2. 가공한 polyester 직물의 K.S. polyester에 대한 대전압이 현저하게 감소하였다. 3. 견직물의 대전성은 흠이 없는데도 불구하고 높게 나왔는데 그 이유로서는 견직물의 결점이 마찰에 약하다는 성질과 마찰에 의한 K.S. 표준검사규격이 마찰에 강한 합성섬유를 대상으로 되어서 견직물에는 부적합한데 있다. 4. 동질섬유직물간의 마찰로 인한 대전압이 이질섬유직물간이 대전압보다 작게 나왔다. 5. 정전기 대전압은 세탁반복에 따라 증가하였다. 6. 많은 조사 결과가 Contact Electrification Series 원칙에 준하고 있는 사실, 즉 series상 피차 멀리 배치될수록 마찰대전압이 높아지고 있었다(Fig. 6 참조). 7. 이러한 조사 결과는 정전기 발생에 관하는 한 혼방사작업에 문제점으로 될 것이다. 8. 또한 견직물 가공에 임해서도 정전기 대전압이 가공으로 인해 증가할 것이라는 문제를 잊어서는 안 된다.