초록
The composition of the base glass was determined to be $Na_2O$ 15, $Fe_2O_3$ 35, $B_2O_3$ 0~20, $P_2O_5$ 30~50 by mole percent. The heating temperature for nucleation was determined by means of thermal expansion curve. Crystalline phases were investigated by X-ray diffraction method and I.R Spectra. Electrical conductivities of glass spec-imens were observed in the temperature range 25~20$0^{\circ}C$ The activation energies of these specimens were caculated. The results obtained were as follows : 1) The limit composition of the melts 15mol% $Na_2O$ 35mole% $Fe_2O_5$ 20mole% $B_2O_3$ 30mole% $P_2O_5$ was able to be formed into desired shapes during cooling, . 2) In the measurement of d. c conductivity($\delta$) on the glasses in the system $15Na_2O-35Fe_2O_3$-$B_2O_3$-(50-x) $P_2O_5$ the values decreased by replacing 5 mole% $P_2O_5$ with $B_2O_3$ 3) The d. c conducties of heat treated samples were increased by replacing $P_2O_5$ with $B_2O_3$ 4) $B_2O_3$ contributed to precipitate crystals such as${\gamma}$-$Fe_2O_3$ $Fe_3O_4$ which had the advantage of electronic conduction in heat treated samples. 5) The slope plotted Log($\delta$) versus 1/T in this glass system was linear in the measured temperature range.