Fatigue Crack Initiation and Propagation at Notches

노치 에서의 피로 균열 발생 과 전파 에 관한 연구

The fatigue limits of crack initiation and propagation on the edge elliptical notched semi-infinite plate under completely reversed fatigue stress are determined theoretically. Assuming that the crack initiation and propagation occur when stress intensity factors of notched plate reach the critical values obtained from critical micro-crack length under plain fatigue limit loading and the threshold stress intensity factory, respectively, the fatigue limits of crack initiation and propagation are obtained. The induced theoretical fatigue limit of crack initiation is expressed in terms of plain fatigue limit, critical micro-crack length and notch shape. The one of crack propagation is in terms of threshold stress intensity factor, plain fatigue limit and notch shape. These theoretical results are showed to be in good agreement of Frost's experimental data.

본 연구에서는 완전 역 피로응력(completely reversed fatgue stress)를 받는 타원 노치에서 균열 발생과 전파에 대한 이론 임계 피로 한도를 응력 세기 계수 개념 을 도입하여 임의의 재질과 임으의 타원 노치 형상에 대해서 적용할 수 있도록 유도하 며 그 결과는 기존 이론보다 Frost의 실험치에 더 잘 일치함을 보이고자 한다.