요소수지접착제(尿素樹脂接着劑)를 사용(使用)한 곰솔 집성재(集成材)의 제조조건(製造條件)이 접착성질(接着性質)에 미치는 영향(影響)

Influence of Adhesion Condition on the Laminated Wood of Pinus thunbergii glued with Urea-formaldhyde Resin

This study was carried out to investigate the block shear strength of the 2ply laminated wood composed of Pinus thunbergii with ureaformaldehyde resin as adhesives according to pressure (6, 9, 12, 15kg/$cm^2$), pressing time(5, 10, 20, 30 hrs.), amount of spread(54, 108, 217, 324g/$cm^2$), hardener(10, 20, 30, 40% of 10% $NH_4CL$ on resin) and extender(0, 5, 10, 15% wheat flour on resin), and the bending strength and bending young's modulus of laminated beam according to the number of ply. The results were summarized as follows; 1. According to pressing pressure with amount of spread 217g/$cm^2$ both dry and wet shear strength of laminated wood showed the highest in 15kg/$cm^2$, and hot-cold soaking treatment showed the highest in 9kg/$cm^2$, while all shear strength of dry, wet and hot-cold soaked laminated wood have been reduced with the increasing of pressing time. 2. According to amount of spread, adhesion strength with the dry, wet and hot-cold soaking treatments revealed the highest in 217g/$cm^2$ and have been reduced under or over 217g/$cm^2$ of spread. 3. According to addition of hardener and extender, all shear strength of laminated block with the dry, wet and hot-cold soaking treatments have been reduced in increasing of addition amount of hardener and extender. The bending strength of beam according to the number of ply showed the highest in 2ply laminated wood and horizontal loading beam to glue line had the higher in strength than the vertical loading.