X-Ray Fluorescence Analysis of $Ta_2O_5, Nb_2O_5, TiO_2, SnO_2$ and $Zr_O2$ in Tin-Slags

주석-슬랙 중 $Ta_2O_5, Nb_2O_5, TiO_2, SnO_2$, 및 $ZrO_2$의 X-선 형광분석

  • Young-Sang Kim (Department of Chemistry, Korea University) ;
  • Chong Wook Lee (Chemical Analysis Laboratory, Korea Advanced Institute of Science and Technology)
  • 김영상 (고려대학교 문리대학 화학과) ;
  • 이종욱 (한국과학기술연구원 화학분석실)
  • Published : 1983.08.20

Abstract

With the synthetic standards, valuable metals $(Ta_2O_5, Nb_2O_5, TiO_2, SnO_2$, and $ZrO_2$) in the tin slags have been determined by the x-ray fluorescence spectrometry. The powder sample and the standards are homogeneously mixed with anhydrous $Li_2B_4O_7$ and La_2O_3$ in weight ratio of 15 : 42 : 3 respectively. The mixed material is fused at $1,150^{\circ}C$ for 30 minutes to be changed into the glass bead. The bead is ground to (-) 325 mesh size and pelletized. The analytical results obtained in this work are consistent with the data obtained by other common methods within allowable error range. The standard deviation for $Ta_2O_5$ in PTS-H sample is 0.12 % at level of 3.40 % content.

합성표준시료를 이용하여 주석슬랙 중 유가금속들인 $Ta_2O_5, Nb_2O_5, TiO_2, SnO_2 $$ZrO_2$를 X-선형광분광법으로 정량하였다. 분석시료와 표준시료분말들을 융제인 무수 $Li_2B_4O_7$$La_2O_3$를 무게비 15:42:3의 비율로 균일하게 혼합한다. 혼합분말을 $1,150^{\circ}C$에서 30분간 용융하여 유리구슬을 만든다. 이 구슬을 325메쉬 이하로 분쇄하여 수압기를 이용 pellet으로 만들어 시편으로 사용한다. 분석결과들은 다른 분석법에 의해 얻은 값들과 허용오차 범위내에서 잘 일치한다. 또 PTS-H시료에 대한 표준편차가 함량 3.40 %에서 0.12 %로 재현성도 좋음을 보여 주었다.

Keywords

References

  1. Appl. Spectrosc. v.22 R. A. Raidly
  2. Anal. Chem. v.41 D. A. Stephenson
  3. Norelco Reptr. v.4 F. Claisse
  4. Appl. Spectrosc. v.17 J. E. Towmend
  5. Advan. X-Ray Anal. v.10 J. O. Larson;R. A. Winkler;J. G. Guffy
  6. Japan Analyst v.17 K. Hisano;K. Oyama
  7. Methods of Quantitative Inorganic Analysis K. Kodama
  8. Colorimetric Determination of Elements G. Charlot
  9. Polarographic Techniques L. Meites